Title
Ispitivanje biokompatibilnosti nanostrukturnih materijala na bazi aktivnih kalcijum silikatnih sistema i hidroksiapatita
Creator
Opačić-Galić, Vanja N., 1969-
Copyright date
2014
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 27.05.2014.
Other responsibilities
mentor
Živković, Slavoljub, 1958-
komentor
Jokanović, Vukoman
član komisije
Vujašković, Mirjana, 1956-
član komisije
Danilović, Vesna, 1962-
član komisije
Mitić-Ćulafić, Dragana, 1960-
Academic Expertise
Medicinske nauke
University
Univerzitet u Beogradu
Faculty
Stomatološki fakultet
Alternative title
Biocompatibility of nanostructural biomaterials based on active calcium silicate systems and hydroxyapatite
Publisher
[V. N. Opačić-Galić]
Format
176 listova
description
Stomatologija - Kliničke stomatološke nauke / Dentistry - Clinical Dental Science
Abstract (sr)
Usavršavanje materijala koji bi mogli da se koriste kao biološke «zamene»
kosti,danas je jedna od najznačajnijih i najaktivnijih oblasti istraživanja
biomaterijala. Biokompatibilnost i bioaktivnost ovih materijala obezbeđuje
interakciju sa biološkim sistemima, a time i obnavljanje funkcije oštećenih tkiva
i/ili organa u ljudskom organizmu...
Poslednjih godina razvijen je veliki broj materijala za endodontsku
primenu, koji osim biokompatibilnosti imaju ulogu i bio-induktora u očuvanju
zdravlja pulpe i periodontalnog tkiva, ali i stimulišu regeneraciju oštećenih
tkiva.
Cilj ovog istraživanja je bio da se proveri biokompatibilnost i
biofunkcionalnost novih nanostrukturnih materijala na bazi kalcijum silikatnih
sistema (CS) i hidroksiapatita (CS-HA).
Prvi korak u ovom istraživanju je bilo analiziranje sastava, određivanje
veličine čestica, merenje vremena vezivanja i određivanje čvrstoće
novosintetisanih materijala.
Strukturu kalcijum silikata čine uglavnom aglomerati veličine nekoliko
mikrometara koji su izgrađeni od manjih partikula (čestica) sa dimenzijama
između 117 i 477nm. Ove partikule su uglavnom sferičnog ili elipsoidnog
oblika, manje ili više izdužene u jednom pravcu. Partikule HA su bile
nepravilnog oblika, većinom okruglaste, sa dimenzijama od 60 nm do 470nm.
EDS analiza je pokazala da je hemijski sastav kalcijum silikata (Ca 22.21, Si
8.22, O 69.7 u atomskim%) odgovarao odnosu Ca/Si od približno 2.7
(atomski%). Vreme vezivanja za CS je započinjalo 3 minuta nakon dodavanja
dejonizovane vode, a kompletno vezivanje se završava nakon 10 minuta. Za CSHA
ove vrednosti su bile 5 i 15 minuta, respektivno.
Za proveru biokompatibilnosti ovih materijala korišćeni su predklinički in
vitro i in vivo testovi.
Abstract (en)
Development of new materials, that could be used as biological bone
"replacement", is today one of the most important and the most active research
areas of biomaterials. Bioactivity and biocompatibility of these materials
provides the interaction with biological systems, and thereby enables restoring
the function of damaged tissues and/or organs in the human body.
In recent years, a large number of materials for endodontic applications
have been developed. Besides biocompatibility, these materials have an
additional role as bio- inducers in health preservation of the periodontal and
pulpal tissue, as well as stimulation of damaged tissues regeneration.
The aim of this study was to examine the biocompatibility and
bioactivity of new nanostructured materials based on calcium silicate systems
(CS) and hydroxyapatites (CS-HA).
The first step in this research was to analyze the composition, particle
sizing, and to determine the setting time and the strength of the newly
synthesized material.
The structure of calcium silicates is mainly composed of agglomerates
with few micrometers in size, which are made of smaller particles with sizes
between 117 and 477nm. These particles are generally spherical or ellipsoidal
shape, more or less elongated in one direction. HA particles were irregular in
shape, mostly rounded, with dimensions of 60 nm to 470nm.
EDS analysis showed that the chemical composition of calcium silicate
(Ca 22.21 , 8.22 Si , O 69.7 in atomic % ) corresponded to the Ca/Si ratio in
about 2.7 (in atomic %). The setting time of the CS began 3 minutes after
addition of deionized water, and the bonding was completed within 10 minutes
after. For HA-CS these values were 5 and 15 minutes, respectively.
To test the biocompatibility of these materials pre-clinical in vitro and in
vivo assays were used...
Authors Key words
nanomaterijali, kalcijum silikatni sistemi, hidroksiapatit,
biokompatibilnost, bioaktivnost
Authors Key words
nanomaterials, calcium silicate systems, hydroxyapatite,
biocompatibility, bioactivity
Classification
615.46:616.314(043.3)
Type
Tekst
Abstract (sr)
Usavršavanje materijala koji bi mogli da se koriste kao biološke «zamene»
kosti,danas je jedna od najznačajnijih i najaktivnijih oblasti istraživanja
biomaterijala. Biokompatibilnost i bioaktivnost ovih materijala obezbeđuje
interakciju sa biološkim sistemima, a time i obnavljanje funkcije oštećenih tkiva
i/ili organa u ljudskom organizmu...
Poslednjih godina razvijen je veliki broj materijala za endodontsku
primenu, koji osim biokompatibilnosti imaju ulogu i bio-induktora u očuvanju
zdravlja pulpe i periodontalnog tkiva, ali i stimulišu regeneraciju oštećenih
tkiva.
Cilj ovog istraživanja je bio da se proveri biokompatibilnost i
biofunkcionalnost novih nanostrukturnih materijala na bazi kalcijum silikatnih
sistema (CS) i hidroksiapatita (CS-HA).
Prvi korak u ovom istraživanju je bilo analiziranje sastava, određivanje
veličine čestica, merenje vremena vezivanja i određivanje čvrstoće
novosintetisanih materijala.
Strukturu kalcijum silikata čine uglavnom aglomerati veličine nekoliko
mikrometara koji su izgrađeni od manjih partikula (čestica) sa dimenzijama
između 117 i 477nm. Ove partikule su uglavnom sferičnog ili elipsoidnog
oblika, manje ili više izdužene u jednom pravcu. Partikule HA su bile
nepravilnog oblika, većinom okruglaste, sa dimenzijama od 60 nm do 470nm.
EDS analiza je pokazala da je hemijski sastav kalcijum silikata (Ca 22.21, Si
8.22, O 69.7 u atomskim%) odgovarao odnosu Ca/Si od približno 2.7
(atomski%). Vreme vezivanja za CS je započinjalo 3 minuta nakon dodavanja
dejonizovane vode, a kompletno vezivanje se završava nakon 10 minuta. Za CSHA
ove vrednosti su bile 5 i 15 minuta, respektivno.
Za proveru biokompatibilnosti ovih materijala korišćeni su predklinički in
vitro i in vivo testovi.
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.