Title
Кинетика кристализације и промене микроструктуре термички третираних аморфних легура на бази гвожђа
Creator
Vasić, Milica M. 1987-
Copyright date
2015
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 09.02.2016.
Other responsibilities
mentor
Minić, Dragica.
član komisije
Adnađević, Borivoj, 1951-
član komisije
Cvjetićanin, Nikola, 1959-
član komisije
Pavlović, Vladimir.
Academic Expertise
Prirodno-matematičke nauke
Academic Title
-
University
Univerzitet u Beogradu
Faculty
Fakultet za fizičku hemiju
Alternative title
Crystallization kinetics and microstructural changes of thermally treated iron-based amorphous alloys.
Publisher
[ М. М. Васић]
Format
VIII, 157 листова
description
Физичка хемија-Физичка хемија материјала / Physical Chemistry-Physical Chemistry of Materials
Abstract (sr)
У овој докторској дисертацији је испитано пет аморфних легура на бази
гвожђа, различитог хемијског састава, са циљем да се код ових легура механизам
и кинетика кристализације појединачних фаза разјасне и повежу са променама
микроструктуре и морфологије, које наступају при загревању. Узорци свих
испитиваних аморфних легура су добијени методом брзог хлађења на ротирајућем
диску. Њихов хемијски састав у ат.% се може представити формулама
Fe73,5Cu1Nb3Si15,5B7, Fe75Ni2Si8B13C2, Fe79,8Ni1,5Si5,2B13C0,5, Fe81B13Si4C2 и
Fe40Ni40P14B6.
Применом инструменталних структурних метода, XRD, Мезбауерове
спектроскопије и електронске дифракције, идентификоване су кристалне фазе које
настају загревањем и одређене су њихове количине, за сваку од легура.
Рендгеноструктурном анализом нађени су микроструктурни параметри
различитих фаза и праћене њихове промене услед изотермског загревања. TEM
снимци узорака легура који су загревани на највишим температурама показују да
су зрна различитих кристалних фаза величина од неколико десетина до неколико
стотина нанометара и неправилних облика, при чему долази до срастања суседних
зрна, на шта су указали и SEM снимци. Морфологија узорака загреваних
неизотермски мења се при промени брзине загревања и максималне температуре
до које се врши загревање, односно зависи од термичке историје узорака, што је
утврђено методама SEM и AFM.
У циљу испитивања термичке стабилности и процеса термичке стабилизације
аморфних легура, примењена је метода диференцијалне скенирајуће
калориметрије. Сложени кристализациони пикови разложени су до појединачних
ступњева одговарајућим математичким поступком, при чему је примена
изоконверзионих метода показала да пикови добијени разлагањем одговарају
процесима који се одвијају у једном ступњу. Појединачни ступњеви су
идентификовани у корелацији са фазним дијаграмима и уоченим...
Abstract (en)
In this dissertation, five iron-based amorphous alloys with different chemical
compositions were examined to clarify the crystallization mechanism and kinetics
corresponding to the formation of individual phases, and to correlate these properties
with the changes in microstructure and morphology, which occur during heating. All of
the examined alloy samples were prepared by using the melt-spinning method. Their
chemical compositions can be represented as follows (at.%): Fe73,5Cu1Nb3Si15,5B7,
Fe75Ni2Si8B13C2, Fe79,8Ni1,5Si5,2B13C0,5, Fe81B13Si4C2, and Fe40Ni40P14B6.
Using structural characterization techniques including XRD, Mössbauer
spectroscopy and electron diffraction, the crystalline phases formed during heating were
identified and their quantities were determined for each of the alloys. XRD analysis
yielded values of microstructural parameters of individual phases, and their changes
induced by isothermal heating were monitored. TEM images of the alloy samples
heated at the highest temperatures showed irregular-shaped grains of different
crystalline phases ranging in size from several tens to several hundreds of nanometers,
with visible coalescence of neighbouring grains, which was observed in SEM
measurements as well. Morphology of non-isothermally treated samples changed with
the heating rate and the maximum heating temperature, that is, it depends on the thermal
history of the sample, which was observed using SEM and AFM methods.
With a view to examining thermal stability of the amorphous alloys and thermal
stabilization processes, differential scanning calorimetry was applied. Complex
crystallization peaks were deconvoluted into individual steps by using appropriate
mathematical procedure, while the application of isoconversional methods showed that
the peaks obtained by deconvolution correspond to single-step processes. Individual
crystallization steps were identified by correlating deconvoluted data with the phase
composition diagrams and the observed microstructural changes, which occur during
heating. Kinetic triplets corresponding to formation of individual crystalline phases
were determined by further analysis, which can be used to predict material lifetime at...
Authors Key words
аморфне легуре, термичка стабилност, кристализација, механизам,
кинетика, деконволуција DSC пикова, ометање раста, морфологија,
микроструктура, магнетна својства
Authors Key words
amorphous alloys, thermal stability, crystallization, mechanism, kinetics,
DSC peak deconvolution, impingement, morphology, microstructure, magnetic
properties.
Type
Tekst
Abstract (sr)
У овој докторској дисертацији је испитано пет аморфних легура на бази
гвожђа, различитог хемијског састава, са циљем да се код ових легура механизам
и кинетика кристализације појединачних фаза разјасне и повежу са променама
микроструктуре и морфологије, које наступају при загревању. Узорци свих
испитиваних аморфних легура су добијени методом брзог хлађења на ротирајућем
диску. Њихов хемијски састав у ат.% се може представити формулама
Fe73,5Cu1Nb3Si15,5B7, Fe75Ni2Si8B13C2, Fe79,8Ni1,5Si5,2B13C0,5, Fe81B13Si4C2 и
Fe40Ni40P14B6.
Применом инструменталних структурних метода, XRD, Мезбауерове
спектроскопије и електронске дифракције, идентификоване су кристалне фазе које
настају загревањем и одређене су њихове количине, за сваку од легура.
Рендгеноструктурном анализом нађени су микроструктурни параметри
различитих фаза и праћене њихове промене услед изотермског загревања. TEM
снимци узорака легура који су загревани на највишим температурама показују да
су зрна различитих кристалних фаза величина од неколико десетина до неколико
стотина нанометара и неправилних облика, при чему долази до срастања суседних
зрна, на шта су указали и SEM снимци. Морфологија узорака загреваних
неизотермски мења се при промени брзине загревања и максималне температуре
до које се врши загревање, односно зависи од термичке историје узорака, што је
утврђено методама SEM и AFM.
У циљу испитивања термичке стабилности и процеса термичке стабилизације
аморфних легура, примењена је метода диференцијалне скенирајуће
калориметрије. Сложени кристализациони пикови разложени су до појединачних
ступњева одговарајућим математичким поступком, при чему је примена
изоконверзионих метода показала да пикови добијени разлагањем одговарају
процесима који се одвијају у једном ступњу. Појединачни ступњеви су
идентификовани у корелацији са фазним дијаграмима и уоченим...
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.