Синтеза и карактеризација везивних материјала на бази алкално активираног електрофилтерског пепела термоелектрана и згуре високе пећи
Creator
Marjanović, Nataša M.
Copyright date
2015
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 05.10.2015.
Other responsibilities
mentor
Petrović, Rada, 1965-
mentor
Komljenović, Miroslav.
član komisije
Janaćković, Đorđe, 1964-
član komisije
Grujić, Snežana, 1964-
član komisije
Petrašinović Stojkanović, Ljiljana.
Academic Expertise
Tehničko-tehnološke nauke
University
Univerzitet u Beogradu
Faculty
Tehnološko-metalurški fakultet
Alternative title
Synthesis and characterization of binding materials based on alkali-activated fly ash and blast furnace slag
Publisher
[Н. М. Марјановић]
Format
209 листова
description
Хемија и хемијска технологија / Chemistry and chemical technology
Abstract (sr)
Извршена је синтеза и карактеризација везивних материјала на бази
алкално активираног индустријског отпадног материјала:
- смеше електрофилтерског пепела и згуре високе пећи и
- механички активираног електрофилтерског пепела.
Синтеза везива на бази алкално активиране смеше електрофилтерског
пепела и згуре високе пећи извршена је употребом раствора натријум-силиката
као активатора, на температури од 95 С у току 24 h и при различитим условима
синтезе: различитим масеним уделима електрофилтерског пепела и згуре високе
пећи (100-0; 75-25; 50-50; 25-75; 0-100), различитим вредностима модула
активатора (SiO2/Na2O: 0,5; 1,0; 1,5) и различитој концентрацији активатора (%
Nа2О: 4; 7; 10). Испитиван је утицај услова синтезе на физичко-механичке и
структурне карактеристике синтетисаних везива. Утврђено је да чврстоће на
савијање и притисак синтетисаних везива у највећој мери зависе од састава смеше
и односа вода/везиво. Време везивања у великој мери зависи од концентрације
активатора, а скупљање при сушењу од температуре реакције у прва 24 сата. На
основу детаљне карактеризације структуре синтетисаних везива закључено је да
продукти реакције алкалне активације у погледу хемијског састава и структуре
зависе од састава смеше. Главни продукт алкалне активације електрофилтерског
пепела је натријум-алумосиликатни гел (N-A-S-H гел). Главни продукти алкалне
активације згуре високе пећи су калцијум-силикохидратни гел са супституцијом
силицијума алуминијумом у структури (C-A-S-H гел) и хидроталкит. При уделу
згуре од 25% у смеши као главни продукт реације формира се N-A-S-H гел са
делимично инкорпорираним Са2+ у структури, или С-N-A-S-H гел. При уделима
згуре од 50-75%, продукти реакције састоје се од C-A-S-H гела и С-N-A-S-H гела
измешених у структури на нанометарском нивоу. Закључено је да је присуство...
Abstract (en)
Synthesis and characterization of binding materials based on alkali-activated
industrial waste material was conducted, involving:
- blends of fly ash and blast furnace slag and
- mechanically activated fly ash.
Synthesis of binders based on alkali-activated blends of fly ash and blast furnace
slag was conducted by use of sodium silicate solution as an activator, at the temperature
of 95 ºC during 24 h, with different synthesis conditions: different fly ash - blast furnace
slag mass ratios (100-0; 75-25; 50-50; 25-75; 0-100), different moduli of the activator
(SiO2/Na2O: 0.5; 1.0; 1.5) and different activator concentration (% Nа2О: 4; 7; 10).
Influence of synthesis conditions on physical-mechanical and structural characteristics
of synthesized binders was investigated. It was found that the flexural and compressive
strengths mostly depended on the composition of the blends and the water/binder ratio.
The setting time highly depended on the activator concentration, while the drying
shrinkage was mostly affected by the reaction temperature during the first 24 h. Based
on detailed structural characterization of the synthesized binders it was concluded that
the chemical composition of alkali activation raction products varied as a function of the
blend composition. The main reaction product of alkali-activated fly ash is sodiumaluminosilicate
gel (N-A-S-H gel). The main reaction product of alkali-activated blast
furnace slag are calcium silicate hydrate gel with substituted silicon by aluminum in the
structure (C-A-S-H gel) and hydrotalcite. With the 25% content of slag in the blend the
N-A-S-H gel with partially incorporated Са2+ in the structure, or С-N-A-S-H gel, was
formed as the main reaction product. With the 50-75% content of slag in the blend the
reaction products comprised of C-A-S-H gel and С-N-A-S-H gel intermixed within the
structure on a nanometer level. It was concluded that the presence of blast furnace slag
in the blend with fly ash affected the improved reactivity of fly ash in the reaction of
alkali activation due to lowering the water/binder ratio and the availability of soluble...
Authors Key words
електрофилтерски пепео, згура високе пећи, алкална активација,
механичка активација, физичко-механичка својства, микроструктура
Authors Key words
fly ash, blast furnace slag, alcali activation, mechanical activation, physicalmechanical
properties, microstructure
Classification
66.017:612.121:666.952:669.162.275.2
Type
Tekst
Abstract (sr)
Извршена је синтеза и карактеризација везивних материјала на бази
алкално активираног индустријског отпадног материјала:
- смеше електрофилтерског пепела и згуре високе пећи и
- механички активираног електрофилтерског пепела.
Синтеза везива на бази алкално активиране смеше електрофилтерског
пепела и згуре високе пећи извршена је употребом раствора натријум-силиката
као активатора, на температури од 95 С у току 24 h и при различитим условима
синтезе: различитим масеним уделима електрофилтерског пепела и згуре високе
пећи (100-0; 75-25; 50-50; 25-75; 0-100), различитим вредностима модула
активатора (SiO2/Na2O: 0,5; 1,0; 1,5) и различитој концентрацији активатора (%
Nа2О: 4; 7; 10). Испитиван је утицај услова синтезе на физичко-механичке и
структурне карактеристике синтетисаних везива. Утврђено је да чврстоће на
савијање и притисак синтетисаних везива у највећој мери зависе од састава смеше
и односа вода/везиво. Време везивања у великој мери зависи од концентрације
активатора, а скупљање при сушењу од температуре реакције у прва 24 сата. На
основу детаљне карактеризације структуре синтетисаних везива закључено је да
продукти реакције алкалне активације у погледу хемијског састава и структуре
зависе од састава смеше. Главни продукт алкалне активације електрофилтерског
пепела је натријум-алумосиликатни гел (N-A-S-H гел). Главни продукти алкалне
активације згуре високе пећи су калцијум-силикохидратни гел са супституцијом
силицијума алуминијумом у структури (C-A-S-H гел) и хидроталкит. При уделу
згуре од 25% у смеши као главни продукт реације формира се N-A-S-H гел са
делимично инкорпорираним Са2+ у структури, или С-N-A-S-H гел. При уделима
згуре од 50-75%, продукти реакције састоје се од C-A-S-H гела и С-N-A-S-H гела
измешених у структури на нанометарском нивоу. Закључено је да је присуство...
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.