Title
Утицај параметара заваривања на својства заварених спојева алуминијумских легура добијених поступком заваривања трењем алатом
Creator
Radisavljević, Igor
Copyright date
2014
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 26.06.2014.
Other responsibilities
mentor
Radović, Nenad, 1964-
član komisije
Cvijović, Zorica, 1951-
član komisije
Romhanji, Endre, 1952-
član komisije
Grabulov, Vencislav, 1953-
član komisije
Živković, Aleksandar, 1975-
Academic Expertise
Tehničko-tehnološke nauke
University
Univerzitet u Beogradu
Faculty
Tehnološko-metalurški fakultet
Alternative title
Influence of welding parameters on joint properties of friction stir welded aluminum alloys
Publisher
[И. Радисављевић]
Format
XIV, 197 листова
description
Техничке науке - Металургија / Technical science - Metallurgy
Abstract (sr)
У раду је испитан УТИЦАЈ ПАРАМЕТАРА ЗАВАРИВАЊА НА СВОЈСТВА
ЗАВАРЕНИХ СПОЈЕВА АЛУМИНИЈУМСКИХ ЛЕГУРА ДОБИЈЕНИХ
ПОСТУПКОМ ЗАВАРИВАЊА ТРЕЊЕМ АЛАТОМ. Коришћене су две
комерцијалне алуминијумске легуре, 5052-Н32 и 2024-Т351, које су испоручене
као плоче дебљљине 8mm. Како би се оценио утицај унете енергије на понашање
материјала и квалитет завареног споја у раду су варирани параметри заваривања,
при чему се однос брзине ротације и брзине заваривања (Vrot/Vzav) кретао од 3,16
до 51,30. Брзина ротације алата износила је 450, 600, 750, 950, 1180 и 1500 obr/min
а брзина заваривања је варирана је од 23 до 380 mm/min. Угао нагиба алата
износио је 10.
Сматра се да однос Vrot/Vzav указује да ли је за дате параметре заваривања могуће
добити спој без присуства грешака, али не и какве ће он механичке
карактеристике поседовати. Резултати ове дисертације указују да се на основу
овог односа може само оријентационо претпоставити понашање споја. Иако се
иста или приближно иста вредност односа Vrot/Vzav може остварити применом
различитих параметара заваривања (нпр. 1180/116=10,17; 950/93=10,21;
750/73=10,27), добијени резултати дају основу да се претпостави да се услови
одигравања процеса заваривања и формирања споја феноменолошки разликују.
Поред односа Vrot/Vzav, велику улогу у добијању споја задовољавајућег квалитета
има величина и константност притисне силе у вертикалном правцу.
Повећање брзине ротације алата (Vrot) има позитиван утицај на механичке
карактеристике завареног споја. Смањење брзине заваривања проузрокује
деградацију изгледа површине споја услед прегоревања материјала. Смањење
брзине заваривања има позитивног ефекта на повећање величине угла савијања
при коме долази до појаве прслине. Резултати одређивања енергије удара указују
да смањење брзине заваривања позитивно утиче на повећње жилавост споја. Са
друге стране при Vrot=1180 obr/min са смањењем брзине заваривања долази до...
Abstract (en)
INFLUENCE OF WELDING PARAMETERS ON JOINT PROPERTIES OF
FRICTION STIR WELDED ALUMINUM ALLOYS was studied in this work. Two
commercial Al alloys 5052-Н32 and 2024-Т351 were received as 8 mm thick plates. In
order to evaluate the influence of heat input during welding on alloys behavior and
properties of weld joint, welding parameters were varied in broadly. Achieved ratio
between rotation and welding speed was between 3,16 and 51,30, i.e. rotation rate was
450, 600, 750, 950, 1180 and 1500 rev/min, while welding speed was between 23 and
380 mm/min. The pin angle was 10. The welded joints were tested by means of both
non-destructive (visual, penetrant and X-ray inspection) and destructive
(metallographic, tension and hardness) testing. In all specimens typical zones are
revealed, with corresponding differences in grain size.
The obtained results suggested that weld appearance was more affected by rotation rate
than by welding speed, due to differences in generated heat level. Increasing R/v ratio
leads to higher, both, heat input (expressed as pseudo-heat index R2/v) and stirring
increment, implying that the behavior is not uniform.
Furthermore, it can be assumed that welding parameters and material flow have
combined effect on weld appearance and they cannot be taken into consideration
separately.
Increasing R/v ratio leads to greater size of weld nugget—width and depth. This is due
to a higher heat input and stirring increment owing to increased R/v ratio. Note that
higher heat input improves material flow around tool pin. In other words, ‘‘revolutions
per one millimeter’’ of the weld metal is increased by increasing R/v ratio. Therefore, a
large amount of frictional heat and plastic-work are produced, and thus material easily
flows and bigger NZ is formed. Different spacing between rings is related to the pin
forward movement per revolution, i.e., at a rotation rate of 750 and 1180 r/min and
welding speed of 116 mm/min. The grain size revealed in the NZ and part of TMAZ is
very fine. It is expected that, during very intensive deformation at high temperature,
grain refinement is introduced by both deformation and recrystallization (static or even...
Authors Key words
заваривање трењем алатом, параметри заваривања,
геометрија алата, квалитет споја, легура 5052, легура
2024
Authors Key words
friction stir welding, welding parameters, tool geometry,
weld quality, alloy 5052, alloy 2024
Classification
621.791 : 691.771
Type
Tekst
Abstract (sr)
У раду је испитан УТИЦАЈ ПАРАМЕТАРА ЗАВАРИВАЊА НА СВОЈСТВА
ЗАВАРЕНИХ СПОЈЕВА АЛУМИНИЈУМСКИХ ЛЕГУРА ДОБИЈЕНИХ
ПОСТУПКОМ ЗАВАРИВАЊА ТРЕЊЕМ АЛАТОМ. Коришћене су две
комерцијалне алуминијумске легуре, 5052-Н32 и 2024-Т351, које су испоручене
као плоче дебљљине 8mm. Како би се оценио утицај унете енергије на понашање
материјала и квалитет завареног споја у раду су варирани параметри заваривања,
при чему се однос брзине ротације и брзине заваривања (Vrot/Vzav) кретао од 3,16
до 51,30. Брзина ротације алата износила је 450, 600, 750, 950, 1180 и 1500 obr/min
а брзина заваривања је варирана је од 23 до 380 mm/min. Угао нагиба алата
износио је 10.
Сматра се да однос Vrot/Vzav указује да ли је за дате параметре заваривања могуће
добити спој без присуства грешака, али не и какве ће он механичке
карактеристике поседовати. Резултати ове дисертације указују да се на основу
овог односа може само оријентационо претпоставити понашање споја. Иако се
иста или приближно иста вредност односа Vrot/Vzav може остварити применом
различитих параметара заваривања (нпр. 1180/116=10,17; 950/93=10,21;
750/73=10,27), добијени резултати дају основу да се претпостави да се услови
одигравања процеса заваривања и формирања споја феноменолошки разликују.
Поред односа Vrot/Vzav, велику улогу у добијању споја задовољавајућег квалитета
има величина и константност притисне силе у вертикалном правцу.
Повећање брзине ротације алата (Vrot) има позитиван утицај на механичке
карактеристике завареног споја. Смањење брзине заваривања проузрокује
деградацију изгледа површине споја услед прегоревања материјала. Смањење
брзине заваривања има позитивног ефекта на повећање величине угла савијања
при коме долази до појаве прслине. Резултати одређивања енергије удара указују
да смањење брзине заваривања позитивно утиче на повећње жилавост споја. Са
друге стране при Vrot=1180 obr/min са смањењем брзине заваривања долази до...
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.