Title
Elasto-plastično ponašanje zavarenog spoja od niskolegiranog čelika povišene čvrstoće u uslovima niskocikličnog zamora
Creator
Bulatović, Srđan M., 1983-
Copyright date
2014
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 10.12.2014.
Other responsibilities
mentor
Sedmak, Aleksandar, 1955-
član komisije
Milović, Ljubica, 1965-
član komisije
Prokić-Cvetković, Radica, 1965-
član komisije
Radaković, Zoran, 1961-
član komisije
Burzić, Zijah.
Academic Expertise
Tehničko-tehnološke nauke
University
Univerzitet u Beogradu
Faculty
Mašinski fakultet
Alternative title
Elastic-plastic behaviour of welded joint of high strength low alloy in conditions of low cycle fatigue
Publisher
[S. M. Bulatović]
Format
165 listova
description
Mašinstvo - Mašinski materijali-Zavarivanje materijala / Mechanical engineering - Mechanical materials-welding materials
Abstract (sr)
Ova doktorska disertacija se bavi proučavanjem ponašanja zavarenog spoja
niskolegiranog čelika povišene čvrstoće NIONIKRAL 70 usled dejstva niskocikličnog
zamora. Kako su u praksi zamarajuća oštećenja veoma zastupljena, akcenat na
prslinama je od velikog značaja. Stoga, najveći deo ovog istraživanja je posvećen
ispitivanju otpornosti na niskociklični zamor čelika Nionikral 70. Važna činjenica je
postojanje značajne plastične deformacije u petlji histerezisa iz koje su konstruisane
ciklično naponsko-deformaciona kriva i kriva deformacija-vek. Pomoću ove dve krive
su izračunate ciklične karakteristike za ocenu ponašanja materijala i parametri
niskocikličnog zamora za proračun zamornog veka.
Zbog sticanja šire slike o nastajanju i razvoju zamornih prslina u zavarenom
spoju, kao heterogenoj strukturi zbog svoje geometrijske nesavršenosti usled
zavarivanja, urađena su ispitivanja pomoću elasto-plastične mehanike loma. Univerzalni
parametar J-integral i njegova kritična vrednost JIc su primenjeni za proračun otpornosti
ka stvaranju prsline. Takođe, parametri mehanike loma su upotrebljeni za ocenu rasta
zamorne prsline karakterističnih zona zavarenog spoja u vidu Parisove relacije koristeći
vezu brzine rasta prsline sa opsegom faktora intenziteta napona na vrhu prsline.
Razlike u svojstvima karakterističnih zona zavarenog spoja su uočene i kod
udarnih ispitivanja što je i dokazano vrednostima žilavosti na različitim temperaturama
odnosno vrednostima prelazne temperature krtosti.
Abstract (en)
This doctoral dissertation studies the behaviour of the welded joint of high
strength low-alloy steel NIONIKRAL 70 due to the effects of low cycle fatigue. In
practice, fatigue damages are very present, that's why the focus is on the cracks is of
great importance. Therefore, most of this research is dedicated to examining the
resistance of steel NIONIKRAL 70 to low cycle fatigue. An important fact is the
existence of significant plastic strain in the hysteresis loop from which are constructed
cyclic stress-strain curve and the fatigue life curve. Using these two curves were
calculated cyclic properties for evaluating material behaviour and low cycle fatigue
parameters for the calculation of fatigue life.
Due to a wider perspective on the initiation and development of fatigue cracks in
welded joints, as heterogeneous structure because of its geometric imperfections due to
welding, tests were performed using the elastic-plastic fracture mechanics. Universal
parameter J-integral and its critical value JIc were applied to calculate the resistance to
crack initiation. Also, the fracture mechanics parameters were used for the evaluation of
the fatigue crack growth for characteristic zones of the welded joints in the form of the
Paris equation using relationship of crack growth rate with stress intensity factor range
at the crack tip.
Differences in the properties of characteristic zones of the welded joint were
observed in impact tests as evidenced by the values of toughness at different
temperatures and the values of the nil-ductility transition temperature.
Authors Key words
niskolegirani čelici povišene čvrstoće, niskociklični zamor, stabilizovana
histereza, zamorna prslina, elasto-plastična mehanika loma
Authors Key words
HSLA steels, low cycle fatigue, stabilized hysteresis loop, fatigue crack,
elastic-plastic fracture mechanics
Classification
621.791.05:620.179.2(043.3)
Type
Tekst
Abstract (sr)
Ova doktorska disertacija se bavi proučavanjem ponašanja zavarenog spoja
niskolegiranog čelika povišene čvrstoće NIONIKRAL 70 usled dejstva niskocikličnog
zamora. Kako su u praksi zamarajuća oštećenja veoma zastupljena, akcenat na
prslinama je od velikog značaja. Stoga, najveći deo ovog istraživanja je posvećen
ispitivanju otpornosti na niskociklični zamor čelika Nionikral 70. Važna činjenica je
postojanje značajne plastične deformacije u petlji histerezisa iz koje su konstruisane
ciklično naponsko-deformaciona kriva i kriva deformacija-vek. Pomoću ove dve krive
su izračunate ciklične karakteristike za ocenu ponašanja materijala i parametri
niskocikličnog zamora za proračun zamornog veka.
Zbog sticanja šire slike o nastajanju i razvoju zamornih prslina u zavarenom
spoju, kao heterogenoj strukturi zbog svoje geometrijske nesavršenosti usled
zavarivanja, urađena su ispitivanja pomoću elasto-plastične mehanike loma. Univerzalni
parametar J-integral i njegova kritična vrednost JIc su primenjeni za proračun otpornosti
ka stvaranju prsline. Takođe, parametri mehanike loma su upotrebljeni za ocenu rasta
zamorne prsline karakterističnih zona zavarenog spoja u vidu Parisove relacije koristeći
vezu brzine rasta prsline sa opsegom faktora intenziteta napona na vrhu prsline.
Razlike u svojstvima karakterističnih zona zavarenog spoja su uočene i kod
udarnih ispitivanja što je i dokazano vrednostima žilavosti na različitim temperaturama
odnosno vrednostima prelazne temperature krtosti.
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.