Title
Korelacija parametara Rheocasting procesa-strukture i svojstva nadeutektičkih aluminijum-silicijum legura
Creator
Ćosić, Milena M., 1968-
Copyright date
2013
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 10.04.2014.
Other responsibilities
mentor
Aćimović-Pavlović, Zagorka S., 1948-
član komisije
Raić, Karlo, 1955-
član komisije
Dojčinović, Marina, 1964-
član komisije
Terzić, Anja
Academic Expertise
Tehničko-tehnološke nauke
University
Univerzitet u Beogradu
Faculty
Tehnološko-metalurški fakultet
Alternative title
The correlation of rheocasting process parameters - structure and properties of hypereutectic aluminium-silicon alloys.
Publisher
[M. M. Ćosić]
Format
167 listova
description
Metalurgija - Livarstvo / Metallurgy - Casting
Abstract (sr)
Nadeutektičke Al-Si legure su našle široku primenu u automobilskoj i avio industriji
zbog odlične otpornosti na koroziju i habanje, niskog koeficijenta termičkog širenja,
dobre čvrstoće, odličine livkosti i male gustine. Svojstva nadeutektičkih Al – Si legura
zavise od karakteristika njihove livene mikrostrukture koja se mogu poboljšati
mikrostrukturnim promenama. U okviru ovog rada poboljšanje mehaničkih svojstava
(tvrdoće) i kavitacione otpornosti realizovani su sledećim promenama: promenom
veličine, morfologije (oblika) i raspodele primarnih i eutektičkih Si čestica.
Da bi se postigla transformacija dendritne u ne-dendritnu strukturu, poluočvrsli rastop
AlSi18CuMgNi legure izlagan je dejstvu smicajnih sila nastalih mehaničkim mešanjem.
Mešanje rastopa legure, primenom mešača oblika ploče, izvedeno je u temperaturnom
intervalu između solidus i likvidus temperature sa postepenim povećanjem brzine
mešanja od 500 do 1500 o/min. Odlivci kompozita AlSi18CuMgNi/SiC dobijeni su
primenom kompokasting postupka. Kao ojačivač korišćen je SiC sa prosečnom
veličinom čestica 30 μm.
Kavitaciona otpornost materijala, kao što su legure metala, zavise od mehaničkih
svojstava posebno tvrdoće. Reokast uzorci dobijeni pri većoj brzini hlađenja i smicanja
pokazali su najveću tvrdoću. Vrednost tvrdoće reokast uzoraka je opadala sa porastom
vremena mešanja usled aglomeracionih procesa. Kavitaciona otpornost konvencionalnih
(gravitaciono kokilno livenje), reokast i odlivaka kompozita procenjena je primenom
ultrazvučne vibracione metode sa stacionarnim uzorkom. Gubitak mase odlivaka za
vreme ispitivanja određivan je analitičkom metodom. Mikrostruktura i morfologija
oštećene površine testiranih materijala ispitivane su primenom optičkog (OM) i
skenirajućeg elektronskog mikroskopa (SEM)...
Abstract (en)
Hypereutectic Al-Si alloys are widely used in the automobile and aerospace industries
because they exhibit excellent wear and corrosion resistance, low coefficient of thermal
expansion, good strength, excellent castability and low density. The properties of
hypereutectic Al-Si alloys depend on the characteristics of their cast microstructure and
they can be improved by microstructure changes. In this paper, the improvements in the
mechanical properties (hardness), cavitation resistance were realized with the following
changes: size, morphology (or shape), and distribution of primary and Si eutectic
particles. The semi-solid melt of the AlSi18CuMgNi alloy was exposed to shear forces
(caused by mechanical mixing) in order to achieve transformation of dendritic into the
non-dendritic structure. Mixing of the melt (active part of the paddle stirrer) was
performed in the temperature range between liquidus and solidus temperatures with a
gradual increase in mixing speed from 500 to 1500 rpm. Aluminium matrix composite
AlSi18CuMgNi/SiC castings were prepared using the compocasting technique. The
reinforcements used were silicon carbide (SiC) particles with an average size of 30 μm.
The cavitation resistance of materials such as metal alloys depends of mechanical
properties (especially hardness) and microstructure. The maximum in hardness for
rheocast sample obtained by higher cooling rate and higher stirring speed was achieved.
The hardness values for rheocast sample decrease with increasing the stirring time due
to agglomeration process. The cavitation resistance of conventional, rheocast and
composite castings was evaluated by using an ultrasonically induced cavitation test
method. Mass loss of castings during testing time was measured by an analytical
method. Microstructures and morphology of damaged surfaces of tested materials were
examined using of optical microscopy (OM) and scanning electron microscopy (SEM)...
Authors Key words
Al –Si legure, reokasting, kompokasting, mikrostruktura, kavitaciona
otpornost
Authors Key words
Al-Si alloys, rheocasting, compocasting, microstructure, cavitation
resistance
Classification
621.74
Type
Tekst
Abstract (sr)
Nadeutektičke Al-Si legure su našle široku primenu u automobilskoj i avio industriji
zbog odlične otpornosti na koroziju i habanje, niskog koeficijenta termičkog širenja,
dobre čvrstoće, odličine livkosti i male gustine. Svojstva nadeutektičkih Al – Si legura
zavise od karakteristika njihove livene mikrostrukture koja se mogu poboljšati
mikrostrukturnim promenama. U okviru ovog rada poboljšanje mehaničkih svojstava
(tvrdoće) i kavitacione otpornosti realizovani su sledećim promenama: promenom
veličine, morfologije (oblika) i raspodele primarnih i eutektičkih Si čestica.
Da bi se postigla transformacija dendritne u ne-dendritnu strukturu, poluočvrsli rastop
AlSi18CuMgNi legure izlagan je dejstvu smicajnih sila nastalih mehaničkim mešanjem.
Mešanje rastopa legure, primenom mešača oblika ploče, izvedeno je u temperaturnom
intervalu između solidus i likvidus temperature sa postepenim povećanjem brzine
mešanja od 500 do 1500 o/min. Odlivci kompozita AlSi18CuMgNi/SiC dobijeni su
primenom kompokasting postupka. Kao ojačivač korišćen je SiC sa prosečnom
veličinom čestica 30 μm.
Kavitaciona otpornost materijala, kao što su legure metala, zavise od mehaničkih
svojstava posebno tvrdoće. Reokast uzorci dobijeni pri većoj brzini hlađenja i smicanja
pokazali su najveću tvrdoću. Vrednost tvrdoće reokast uzoraka je opadala sa porastom
vremena mešanja usled aglomeracionih procesa. Kavitaciona otpornost konvencionalnih
(gravitaciono kokilno livenje), reokast i odlivaka kompozita procenjena je primenom
ultrazvučne vibracione metode sa stacionarnim uzorkom. Gubitak mase odlivaka za
vreme ispitivanja određivan je analitičkom metodom. Mikrostruktura i morfologija
oštećene površine testiranih materijala ispitivane su primenom optičkog (OM) i
skenirajućeg elektronskog mikroskopa (SEM)...
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.