Title
Sinteza, struktura i svojstva biodegradibilnih alifatskih poli(estar etara)
Creator
Stamenić, Dragana S. 1977-
Copyright date
2014
Object Links
Select license
Bez licence - direktna primena zakona
License description
Ako ne izaberete neku od licenci, vaše zaštićeno delo može biti korišćeno samo u okviru opštih ograničenja autorskih prava. Na taj način ne dozvoljavate komercijalno ni nekomercijalno korišćenje, naročito reprodukciju, distribuciju, emitovanje, dostupnost i obradu dela. Izbor Creative Commons (CC) licence promoviše diseminaciju vašeg dela. Za više informacija: http://creativecommons.org.rs/licence
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 03.07.2014.
Other responsibilities
mentor
Đonlagić, Jasna
član komisije
Jeremić, Katarina, 1950-
član komisije
Nikolić, Marija, 1973-
član komisije
Pilić, Branka, 1966-
član komisije
Dunjić, Branko
Academic Expertise
Tehničko-tehnološke nauke
University
Univerzitet u Beogradu
Faculty
Tehnološko-metalurški fakultet
Alternative title
Synthesis, structure and properties of biodegradable aliphatic poly(ester ether)s.
Publisher
[D. S. Stamenić]
Format
XIII, 198 listova
description
Hemija i hemijska tehnologija - Hemija makromolekula / Chemical technology - Chemistry macromolecules
Abstract (sr)
U ovom doktorskom radu su sintetisani i izuĉavani alifatski mulitblok poli(estar etri) sa
ciljem da se razviju novi biodegradabilni polimerni materijali koji istovremeno poseduju
elastomerna svojstva, kao i laku preradljivost koja je odlika termoplastiĉnih polimera.
Elastiĉna svojstva potiĉu od dugaĉkih amorfnih mekih segmenta, dok kratki kristališući
tvrdi segmenati obezbeĊuju polimeru odgovarajuću jaĉinu. Alifatski poliestri spadaju u
grupu biodegradabilnih polimera koji su podloţni enzimskoj degradaciji ĉiji produkti
razgradnje (dioli, kiseline i hidroksi kiseline) nisu toksiĉni i ulaze u metaboliĉke procese
mikroorganizama. Biodegradabilnost zavisi od hemijske strukture, odnosa hidrofobnosti
i hidrofilnosti, krutosti polimernih lanaca, kristalne strukture i stepena kristaliniĉnosti
koji ima najveći uticaj na biodegradaciju. Biodegradabilna svojstva poliestara se mogu
poboljšati povećanjem hidrofilnosti ugradnjom mekih hidrofilnih segmenata (npr.
polietri) u polimerne lance.
Biodegradabilni multiblok kopolimeri poli(estar etri) su sintetisani na bazi tvrdih
poliestarskih segmenata poli(butilen sukcinata) (PBS), i dva razliĉita hidrofilna meka
polietarska segmenta poli(etilen oksida) (PEO) i poli(tetrametilen oksida) (PTMO).
Udeo mekih segmenata u kopolimerima je variran od 10 do 50 mas.%. Izuĉavan je
uticaj razliĉitih mekih segmenata na strukturu, fiziĉke karakteristike, kao i na enzimsku
i hidrolitiĉku degradaciju sintetisanih poli(estar etara).
Poli(estar etri) su sintetisani dvostepenom reakcijom polikondenzacije u rastopu iz
dimetil-sukcinata, 1,4-butandiola i polietara PEO (Mn=1000 g/mol) u prvoj seriji,
odnosno PTMO (Mn=1000 g/mol) u drugoj seriji kopolimera, u prisustvu efikasnog
katalizatora titan-tetrabutoksida (Ti(OC4H9)4) i bez dodatka termiĉkog stabilizatora.
Struktura i sastav sintetisanih kopolimera, kao i proseĉna duţina tvrdih segmenata su
odreĊeni 1 H NMR spektroskopijom. 1H NMR analizom je potvrĊena struktura
sintetisanih kopolimera, a sastav poli(estar etara) je bio u dobrom slaganju sa sastavom
polazne reakcione smeše. Vrednosti proseĉnog stepena polimerizacije tvrdih PBS
segmenata u kopolimernim lancima ukazuju na smanjenje duţine tvrdih segmenata sa
porastom udela inkorporiranih mekih polietarskih segmenata...
Abstract (en)
In this dissertation were synthesized and studied aliphatic multiblock poly(ester ether)s
with aim of developing biodegradable polymeric materials which also possess
elastomeric properties and easy processability which is characteristic of thermoplastic
polymers. Elastic behavior of these polymers originate from long amorphous soft
segments, while short crystallizable hard segments provide great impact strength.
Aliphatic polyesters belong to the group of biodegradable polymers susceptible to
biological attack which products of biodegradation (diols, acids and hydroxy acids) are
not toxic and are a part of the metabolic processes of microorganisms. Biodegradability
depends on chemical structure, ratio of hydrophobicity to hydrophilicity, stiffness of the
polymer chains, crystal structure and degree of crystallinity which has the greatest
influence on degradation. The biodegradable properties of polyesters can be improved
through increasing the hydrophilicity by the introduction of hydrophilic segments (e.g.
polyethers) into the backbone of the polymer chains.
Biodegradable multiblock poly(ester ether)s based on poly(butylene succinate) as the
hard segment and two different hydrophilic polyethers soft segments poly(ethylene
oxide) (PEO) in the first series, and poly(tetramethylene oxide) (PTMO) in the second
series were synthesized. The content of soft segments was varied from 10 to 50 mass%.
The effect of the introduction of different polyether soft segments on the structure,
physical properties, as well as on enzymatic and hydrolytic degradation was
investigated.
The poly(ester ether)s were synthesized by two stage melt polycondensation reaction
from dimethyl succinate, 1,4-butanediol and PEO (Mn =1000 g/mol) in the first series,
and PTMO (Mn =1000 g/mol) in the second series in the presence of a highly effective
catalyst, tetra-n-butyl-titanate (Ti(OBu)4) and without the addition of a heat stabilizer...
Authors Key words
segmentirani termoplastiĉni elastomeri, poli(estar etri), sinteza kopolimera,
poli(butilen sukcinat), poli(etilen oksid), poli(tetrametilen oksid), hidrolitiĉka degradacija,
in vitro enzimska degradacija, Candida rugosa lipaza
Authors Key words
segmented thermoplastic elastomers, poly(ester ether)s, copolymer synthesis,
poly(butylene succinate), poly(ethylene oxide), poly(tetramethylene oxide), hydrolytic
degradation, in vitro enzymatic degradation, Candida rugosa lipase
Classification
577.1
Type
Tekst
Abstract (sr)
U ovom doktorskom radu su sintetisani i izuĉavani alifatski mulitblok poli(estar etri) sa
ciljem da se razviju novi biodegradabilni polimerni materijali koji istovremeno poseduju
elastomerna svojstva, kao i laku preradljivost koja je odlika termoplastiĉnih polimera.
Elastiĉna svojstva potiĉu od dugaĉkih amorfnih mekih segmenta, dok kratki kristališući
tvrdi segmenati obezbeĊuju polimeru odgovarajuću jaĉinu. Alifatski poliestri spadaju u
grupu biodegradabilnih polimera koji su podloţni enzimskoj degradaciji ĉiji produkti
razgradnje (dioli, kiseline i hidroksi kiseline) nisu toksiĉni i ulaze u metaboliĉke procese
mikroorganizama. Biodegradabilnost zavisi od hemijske strukture, odnosa hidrofobnosti
i hidrofilnosti, krutosti polimernih lanaca, kristalne strukture i stepena kristaliniĉnosti
koji ima najveći uticaj na biodegradaciju. Biodegradabilna svojstva poliestara se mogu
poboljšati povećanjem hidrofilnosti ugradnjom mekih hidrofilnih segmenata (npr.
polietri) u polimerne lance.
Biodegradabilni multiblok kopolimeri poli(estar etri) su sintetisani na bazi tvrdih
poliestarskih segmenata poli(butilen sukcinata) (PBS), i dva razliĉita hidrofilna meka
polietarska segmenta poli(etilen oksida) (PEO) i poli(tetrametilen oksida) (PTMO).
Udeo mekih segmenata u kopolimerima je variran od 10 do 50 mas.%. Izuĉavan je
uticaj razliĉitih mekih segmenata na strukturu, fiziĉke karakteristike, kao i na enzimsku
i hidrolitiĉku degradaciju sintetisanih poli(estar etara).
Poli(estar etri) su sintetisani dvostepenom reakcijom polikondenzacije u rastopu iz
dimetil-sukcinata, 1,4-butandiola i polietara PEO (Mn=1000 g/mol) u prvoj seriji,
odnosno PTMO (Mn=1000 g/mol) u drugoj seriji kopolimera, u prisustvu efikasnog
katalizatora titan-tetrabutoksida (Ti(OC4H9)4) i bez dodatka termiĉkog stabilizatora.
Struktura i sastav sintetisanih kopolimera, kao i proseĉna duţina tvrdih segmenata su
odreĊeni 1 H NMR spektroskopijom. 1H NMR analizom je potvrĊena struktura
sintetisanih kopolimera, a sastav poli(estar etara) je bio u dobrom slaganju sa sastavom
polazne reakcione smeše. Vrednosti proseĉnog stepena polimerizacije tvrdih PBS
segmenata u kopolimernim lancima ukazuju na smanjenje duţine tvrdih segmenata sa
porastom udela inkorporiranih mekih polietarskih segmenata...
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.