Title
Морфолошка анализа оштећења ватросталних материјала изложених термошоку
Creator
Dimitrijević, Marija, 1979-
Copyright date
2013
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 05.12.2013.
Other responsibilities
mentor
Jančić Heinemann, Radmila, 1965-
član komisije
Volkov-Husović, Tatjana, 1964-
član komisije
Mitraković, Dragan, 1952-
član komisije
Matović, Branko
član komisije
Rakin, Marko
Academic Expertise
Tehničko-tehnološke nauke
University
Univerzitet u Beogradu
Faculty
Tehnološko-metalurški fakultet
Alternative title
Мorphological analysis of refractories exposed to damage thermal shock.
Publisher
[М. М. Димитријевић]
Format
175 листова
description
Хемија и хемијска технологија / Chemistry and chemical technology
Abstract (sr)
Најважнијa својства ватросталних материјала јесу ватросталност, радна
температура и термичка стабилност. Да би се побољшала физичка и механичка
својства ватросталних материјала базираних на алуминијум оксиду, алуминијум
оксидна влакна су додата у малим количинама према познатом саставу
ватросталног материјала.
Термичка стабилност узорака на бази алуминијум оксида одређивана је
коришћењем стандардне лабораторијске процедуре (SRPS B. D8. 319). Анализа
слике коришћена је за мерење расподеле дужине и пречника влакана, хомогености
влакана у матрици, одређивање удела порозности материјала и мерење и
карактерисање површинског оштећења током испитивања термичке стабилности.
Скенирајућа електронска микроскопија коришћена је за поређење микроструктуре
узорака као и за утврђивање удела порозности у узорцима.
Стандарно испитивање компресијом коришћено је за одређивање притисне
чврстоће и Јунговог модула еластичности. Резултати добијени на основу
термошока и механичких мерења употребљени су за успостављање модела
регресионе анализе која је корелисана са својствима узорака и процесним
параметрима.
Облици површинских оштећења посматрани су у зависности од броја
циклуса излагања термошоку. Параметри облика одређени су алатима за анализу
слике. Утицај услова припреме узорака на морфологију оштећења површине
узорака је проучаван коришћењем статистичке методе анализе главних
компоненти. Показано је да се морфолошки параметри оштећења веома разликују
према саставу и условима припреме керамичких материјала...
Abstract (en)
The most important properties usually determined for refractories are
refractoreness, working temperature and thermal stability. In order to improve the
physical and mechanical properties of alumina based refractories, alumina fibers were
added in small amount to the known refractory composition.
Image analysis was used to measure the fiber lengths distribution, homogeneity
of fiber distribution in the matrix and finally the measurement during thermal stability
testing. Image analysis tools were used for deterioration monitoring of samples before,
during and after each cycle of water quench test.
Thermal stability of the alumina based samples was measured using standard
laboratory procedure (SRPS B. D8. 319), water quench test. Mechanical characteristics
such as strength, dynamic modulus of elasticity resulting from resonance frequency
measurements, as well as ultrasonic velocity were considered.
SEM technique was used to compare the microstructure of specimens and the
observed images gave the porosity in the specimens. Standard compression test was
used to determine the modulus of elasticity and compression strength. Results obtained
from thermal shock testing and mechanical properties measurements were used to
establish regression models that correlated specimen properties to process parameters.
Surface defects were monitored using image analysis tools. Their size and other
morphological parameters were measured using standard image analysis procedures.
The influence of preparation conditions on the surface defects morphology was studied
using principle component analysis. It was shown that morphological parameters of
defects vary corresponding to the composition and preparation conditions of ceramic
material.
Authors Key words
композити, алуминијум оксидна влакна, анализа слике,
термостабилност, електронска микроскопија, метода коначних елемената, анализа
главних компоненти
Authors Key words
composites, alumina fibers, image analysis, termostability, electron
microscopy, finite element method, principal component analysis
Classification
669.018.44
Type
Tekst
Abstract (sr)
Најважнијa својства ватросталних материјала јесу ватросталност, радна
температура и термичка стабилност. Да би се побољшала физичка и механичка
својства ватросталних материјала базираних на алуминијум оксиду, алуминијум
оксидна влакна су додата у малим количинама према познатом саставу
ватросталног материјала.
Термичка стабилност узорака на бази алуминијум оксида одређивана је
коришћењем стандардне лабораторијске процедуре (SRPS B. D8. 319). Анализа
слике коришћена је за мерење расподеле дужине и пречника влакана, хомогености
влакана у матрици, одређивање удела порозности материјала и мерење и
карактерисање површинског оштећења током испитивања термичке стабилности.
Скенирајућа електронска микроскопија коришћена је за поређење микроструктуре
узорака као и за утврђивање удела порозности у узорцима.
Стандарно испитивање компресијом коришћено је за одређивање притисне
чврстоће и Јунговог модула еластичности. Резултати добијени на основу
термошока и механичких мерења употребљени су за успостављање модела
регресионе анализе која је корелисана са својствима узорака и процесним
параметрима.
Облици површинских оштећења посматрани су у зависности од броја
циклуса излагања термошоку. Параметри облика одређени су алатима за анализу
слике. Утицај услова припреме узорака на морфологију оштећења површине
узорака је проучаван коришћењем статистичке методе анализе главних
компоненти. Показано је да се морфолошки параметри оштећења веома разликују
према саставу и условима припреме керамичких материјала...
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.