Title
Имобилизација олова и хрома геополимерима на бази електрофилтерског пепела термоелектрана
Creator
Nikolić, Violeta M. 1978-
Copyright date
2016
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Committee report
Theses Type
Doktorska disertacija
description
Datum odbrane: 28.09.2016.
Other responsibilities
mentor
Petrović, Rada 1965-
mentor
Komljenić, Miroslav
član komisije
Grujić, Snežana, 1964-
član komisije
Miladinović, Zoran
Academic Expertise
Tehničko-tehnološke nauke
University
Univerzitet u Beogradu
Faculty
Tehnološko-metalurški fakultet
Alternative title
Immobilization of lead and chromium by fly ash based geopolymers.
Publisher
[В. Николић]
Format
XXIV, 218 листова
description
Хемија и хемијска технологија / Chemistry and chemical technology
Abstract (sr)
Геополимери су синтетисани алкалном активацијом електрофилтерског
пепела (ЕФП), коришћењем раствора натријум-силиката модула 1,5, при чему је
извршена оптимизација услова синтезе. Оптимизација услова синтезе
геополимера је подразумевала испитивање утицаја температуре (55, 80, 95 C) и
времена реакције (4, 8, 16 и 24 h) на чврстоће геополимера. Утврђено је да постоји
јасна корелација између карактеристика ЕФП, услова синтезе и чврстоћа
геополимера. На основу вредности максималних и минималних чврстоћа при
притиску геополимера извршен је избор ЕФП и одговарајућих геополимера за
даље испитивање процеса имобилизације олова и хрома. Геополимер
максималних чврстоћа при притиску, синтетисан је на бази ЕФП, који се показао
као најреактивнији током алкалне активације, односно поседује највећи садржај
честица мањих од 43 m, стакласте фазе, као и растворљивог силицијума и
алуминијума у јако алкалној средини. С друге стране, геополимер минималних
чврстоћа при притиску, синтетисан је на бази ЕФП који је мање реактиван, тј.
поседује мањи садржај честица мањих од 43 m, стакласте фазе и растворљивог
силицијума и алуминијума. Геополимери на бази изабраних полазних ЕФП
представљали су референтни систем у даљим истраживањима и синтетисани су на
собној температури (20 oC), а време реакције је износило 28 дана...
Abstract (en)
Geopolymers were synthesized by alkali activation of fly ash (FA), using
sodium silicate solution with modulus 1.5, whereby optimization of the synthesis
conditions was performed. Optimization of geopolymers synthesis conditions implied
the investigation of the effect of temperature (55, 80 and 95 °C) and reaction time (4, 8,
16 and 24 h) on the geopolymers strength. It was found that there was a correlation
between FA characteristics, synthesis conditions, and strength of geopolymers. The
selection of FA samples and corresponding geopolymers for further investigation of
chromium and lead immobilization was performed based on the maximum and
minimum values of the geopolymers compressive strength. Geopolymer with the
maximum compressive strength was synthesized of the most reactive FA in the reaction
of alkali activation i.e. which had the highest content of particles smaller than 43 m,
glassy phase, and soluble silicon and aluminum in a strongly alkaline medium. On the
other hand, geopolymer with minimum compressive strength was synthesized of less
reactive FA, which had lower content of particles smaller than 43 m, glassy phase, and
soluble silicon and aluminum. Geopolymers based on selected FA samples represented
the reference system in further research and were synthesized at room temperature (20
°C) with the reaction time of 28 days...
Authors Key words
електрофилтерски пепео, геополимери, алкална активација,
механичка активација, имобилизација, хром, олово
Authors Key words
fly ash, geopolymer, alkali activation, mechanical activation,
immobilization, lead, chromium
Type
Tekst
Abstract (sr)
Геополимери су синтетисани алкалном активацијом електрофилтерског
пепела (ЕФП), коришћењем раствора натријум-силиката модула 1,5, при чему је
извршена оптимизација услова синтезе. Оптимизација услова синтезе
геополимера је подразумевала испитивање утицаја температуре (55, 80, 95 C) и
времена реакције (4, 8, 16 и 24 h) на чврстоће геополимера. Утврђено је да постоји
јасна корелација између карактеристика ЕФП, услова синтезе и чврстоћа
геополимера. На основу вредности максималних и минималних чврстоћа при
притиску геополимера извршен је избор ЕФП и одговарајућих геополимера за
даље испитивање процеса имобилизације олова и хрома. Геополимер
максималних чврстоћа при притиску, синтетисан је на бази ЕФП, који се показао
као најреактивнији током алкалне активације, односно поседује највећи садржај
честица мањих од 43 m, стакласте фазе, као и растворљивог силицијума и
алуминијума у јако алкалној средини. С друге стране, геополимер минималних
чврстоћа при притиску, синтетисан је на бази ЕФП који је мање реактиван, тј.
поседује мањи садржај честица мањих од 43 m, стакласте фазе и растворљивог
силицијума и алуминијума. Геополимери на бази изабраних полазних ЕФП
представљали су референтни систем у даљим истраживањима и синтетисани су на
собној температури (20 oC), а време реакције је износило 28 дана...
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.