Title
Strukturne i termijske karakteristike mehanohemijski tretiranih metalnih prahova
Creator
Zdujić, Miodrag V.
Copyright date
1995
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 24.04.1996.
Other responsibilities
mentor
Poleti, Dejan
član komisije
Skala, Dejan
član komisije
Radmilović, Velimir
član komisije
Karanović, Ljiljana
Academic Expertise
Tehničko-tehnološke nauke
University
Univerzitet u Beogradu
Faculty
Tehnološko-metalurški fakultet
Alternative title
Structural and thermal characteristics of mechanochemically treated metal powders
Publisher
[M. Zdujić]
Format
PDF/A (179 listova)
description
Hemijska tehnologija - nauka o materijalima / Chemical technology - material science
Abstract (sr)
U ovom radu je ispitivano dobijanje neravnotežnin struktura u metalima
mehanohemijskim tretmanom. Strukturne i termijske karakteristike prahova mehanohemijski
tretiranih različito vreme mlevenja su ispitivane rendgenskom strukturnom analizom,
diferencijalnom skanirajućom kalorimetrijom, diferencijalnom termijskom analizom, kao i
skanirajućom i transmisionom elektronskom mikroskopijom. Eksperimentalni rezultati su
diskutovani sa kinetičkog i termodinamičkog stanovišta.
Mehanohemijski tretmani, tj. mehaničko legiranje smeša čistih prahova aluminijuma i
molibdena različitih početnih sastava (Al-0, 3, 10, 17, 20, 27, 50, 75 i 100 at.%Mo) su rađeni u
horizontalnom kugličnom mlinu. U svim sličajevima mlevenje proizvodi nanokristalnu i/ili
amorfnu strukturu. Tokom naknadnog termijskog tretmana, ovakvi metastabilni proizvodi lako
reaguju obrazujući intermetalna jedinjenja: Al12Mo, Al5Mo, Al4Mo, AlgMo3 i AlMo3.
Smesa prahova nikla i molibdena (Ni-50 at.%Mo) je mlevena u različitim tipovima
mlinova. Mehaničkim legiranjem u horizontalnom kuglicnom mlinu dobija se amorfna faza. U
planetarnom i vibracionom mlinu, zbog veće energije mlevenja, dobija se neuređeno
intermetalno jedinjenje.
Mehanohemijska reakcija amortizacije u oba ispitivana sistema je slična i odvija se u
četiri stupnja: (i) obrazovanje veoma finog kompozitnog praha, (ii) obrazovanje čvrstog
rastvora Al(Mo) ili Ni(Mo), (iii) transformacija presićenog čvrstog rastvora u amorfnu fazu i (iv)
postepeno rastvaranje zaostalih kristalita molibdena u amorfnoj matrici.
Abstract (en)
In this study the formation of non-equilibrium structures in metals by mechanochemical
treatment has been investigated. The structural and thermal properties of powders
mechanochemically treated for various milling times have been studied by X-ray
diffraction, differential scanning calorimetry, differential thermal analysis, as well as
scanning and transmission electron microscopy. The experimental results were
discussed from kinetic and thermodynamic point of view.
Mechanochemical treatment, i.e. mechanical alloying of mixture of aluminium and
molybdenum powders of various starting compositions (Al-O, 3, 10, 17, 20, 27, 50, 75
and 100 at.%Mo) was performed in a horizontal ball mill. In all cases milling produced
nanocrystalline or/and amorphous structures. During subsequent heat treatment such
metastable products easily react leading to the formation of intermetallic phases:
Al12Mo, Al5Mo, Al4Mo, Al8Mo3 and AlMo3.
Mixture of nickel and molybdenum powders (Ni-50 at.%Mo) was treated in various
types of mills. Mechanical alloying in the horizontal ball mill yields an amorphous phase
while in planetary and vibrating ball mill a disordered intermetallic compound was
produced as a result of greater milling energies.
The formation of amorphous phase in both systems is similar and occurs in four
stages: (i) formation of very fine composite powders, (ii) formation of solid solution
either Al(Mo) or Ni(Mo), (iii) collapse of supersaturated solid solution into the
amorphous phase and (iv) gradual dissolution of residual molybdenum crystallites into
the amorphous matrix.
Authors Key words
mehanohemijski tretman, mehaničko legiranje, mlevenje, reakcije u čvrstom
stanju, nanokristalni materijali, amorfna faza, sistem Al-Mo, sistem Ni-Mo, intermetalna
jedinjenja, metastabilne strukture
Authors Key words
mechanochemical treatment, mechanical alloying, milling, solid state
reactions, nanocrystalline materials, amorphous phase, Al-Mo system, Ni-Mo system,
intermetallics, metastable structures
Classification
669-4:669.018(043.3)
Subject
Metalni prahovi
Type
Tekst
Abstract (sr)
U ovom radu je ispitivano dobijanje neravnotežnin struktura u metalima
mehanohemijskim tretmanom. Strukturne i termijske karakteristike prahova mehanohemijski
tretiranih različito vreme mlevenja su ispitivane rendgenskom strukturnom analizom,
diferencijalnom skanirajućom kalorimetrijom, diferencijalnom termijskom analizom, kao i
skanirajućom i transmisionom elektronskom mikroskopijom. Eksperimentalni rezultati su
diskutovani sa kinetičkog i termodinamičkog stanovišta.
Mehanohemijski tretmani, tj. mehaničko legiranje smeša čistih prahova aluminijuma i
molibdena različitih početnih sastava (Al-0, 3, 10, 17, 20, 27, 50, 75 i 100 at.%Mo) su rađeni u
horizontalnom kugličnom mlinu. U svim sličajevima mlevenje proizvodi nanokristalnu i/ili
amorfnu strukturu. Tokom naknadnog termijskog tretmana, ovakvi metastabilni proizvodi lako
reaguju obrazujući intermetalna jedinjenja: Al12Mo, Al5Mo, Al4Mo, AlgMo3 i AlMo3.
Smesa prahova nikla i molibdena (Ni-50 at.%Mo) je mlevena u različitim tipovima
mlinova. Mehaničkim legiranjem u horizontalnom kuglicnom mlinu dobija se amorfna faza. U
planetarnom i vibracionom mlinu, zbog veće energije mlevenja, dobija se neuređeno
intermetalno jedinjenje.
Mehanohemijska reakcija amortizacije u oba ispitivana sistema je slična i odvija se u
četiri stupnja: (i) obrazovanje veoma finog kompozitnog praha, (ii) obrazovanje čvrstog
rastvora Al(Mo) ili Ni(Mo), (iii) transformacija presićenog čvrstog rastvora u amorfnu fazu i (iv)
postepeno rastvaranje zaostalih kristalita molibdena u amorfnoj matrici.
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.