Title
Struktura i svojstva višeslojnih Al-Mg traka dobijenih hladnim valjanjem
Creator
Alil, Ana B., 1985-
Copyright date
2018
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 18.05.2018
Other responsibilities
mentor
Popović, Miljana, 1965-
član komisije
Romhanji, Endre, 1952-
član komisije
Radetić, Tamara.
član komisije
Bajat, Jelena, 1964-
član komisije
Burzić, Zijah.
Academic Expertise
Tehničko-tehnološke nauke
University
Univerzitet u Beogradu
Faculty
Tehnološko-metalurški fakultet
Alternative title
Structure and properties of Al-Mg alloy sheets produced by accumulative roll bonding.
Publisher
[A. B. Alil]
Format
183 lista
description
Metalurško inženjerstvo / Metallurgical Engineering
Abstract (sr)
Ispitivan je uticaj akumulativnog spajanja valjanjem (ARB postupak) i konvencionalnog hladnog valjanja (CR postupak) na mehanička i koroziona svojstva standardne AA5083 legure sa 4.2 mas. % Mg i modifikovane legure, sa sadržajem Mg od 5.1 mas.% i dodatkom 0.5 mas.% Zn. Rezultati ispitivanja jednoosnim zatezanjem pokazali su da dolazi do značajnog povećanja parametara čvrstoće i smanjenja
izduženja nakon svakog ARB provlaka i sa porastom stepena deformacije CR postupkom. Pokazana je prednost ARB postupka nad klasičnim postupkom hladnog
valjanja obzirom da se mogu postići veći stepeni deformacije i veća rafinacija strukture.
Pokazano je da povišen sadržaj Mg doprinosi porastu čvrstoće, dok se potencijal za ojačavanje i koroziona otpornost smanjuju. Viši nivo čvrstoće CR traka rezultat je veće gustine dislokacija i izraženijeg deformacionog ojačavanja zbog intenzivnije interakcije dislokacija kod konvencionalnog valjanja u odnosu na ARB postupak. Rezultati testa gubitka mase (NAMLT) pokazali su otpornost jednoslojnih CR i višeslojnih ARB traka ispitivanih legura prema intergranularnoj koroziji (IGC) u deformisanom stanju. Međutim, nakon 7 dana senzitizacije na 100 i 150 °C, CR uzorci AA5083 legure postaju
osetljivi, dok ARB uzorci ostaju otporni prema IGC. Za razliku od standardne legure, CR i ARB trake modifikovane legure pokazale su veliku osetljivost prema IGC nakon tretmana senzitizacije. Osetljivost prema IGC u korelaciji je sa različitom morfologijom i raspodelom β-faze (Mg2Al3) istaložene tokom senzitizacije. Otkriveno je da postojanje smicajnih traka usled intenzivne plastične deformacije u višeslojnoj ARB strukturi, i
pasivnog filma između slojeva doprinosi povoljnoj raspodeli β-faze u strukturi otpornih ARB uzoraka što su potvrdili i rezultati elektrohemijskih ispitivanja. U slučaju IGC osetljivih CR uzoraka, velika količina β-faze istaložena je duž granica zrna.
Elektrohemijski parametri su u dobroj korelaciji sa rezultatima NAML testa, koji su
potvrdili prednost ARB višeslojne strukture u odnosu na konvencionalno hladno
valjanu, i ustanovljeno je da ARB postupak ima realnu mogućnost praktične industrijske
primene za izradu višeslojnih traka jer omogućava transformaciju Al-Mg legura u materijale novih, pobolјšanih svojstava.
Abstract (en)
Influence of accumulative roll bonding (ARB) and conventional cold rolling (CR) on the mechanical and corrosion properties of an AA5083 type alloy with 4.2 wt%
Mg and a modified alloy with 5.1 wt% Mg and addition of 0.5 wt% Zn was studied. Tensile tests showed significant increase in strength and a decrease in elongation after
each ARB deformation and cold rolling reductions. The advantage of ARB processing
over conventional cold rolling was due to the possibility to achieve high degree of deformation and a grain structure refinement. Higher Mg content in a modified AA5083 alloy contributed significantly to the increase in strength, while strain hardening
potential and corrosion resistance were reduced. The higher strength level of cold rolled material was attributed to higher dislocation density and the hardening effect due to more intensive dislocation interactions compared to ARB processed material. Results of nitric acid mass loss test (NAMLT) revealed that cold rolled (CR) monometal and ARB processed multilayered specimens were resistant toward intergranular corrosion (IGC) in as-deformed state. However, after 7 days of sensitization at 100 and 150 °C, CR material of AA5083 alloy became IGC sensitive, while ARB specimens stayed resistant.
On the other hand, both cold rolled and ARB processed specimens of a modified alloy became IGC susceptible after sensitization. IGC susceptibility of the tested alloys can be correlated with different morphology and distribution of β-phase (Mg2Al3)
precipitated during sensitization. It was found that an extensive shear banding within ARB multilayered structure and the existence of passive film between the layers contributed a favorable distribution of β-phase in the structure of IGC resistant ARB specimens. In case of IGC susceptible cold rolled specimens, large amount of β-phase precipitated preferentially along the elongated grain boundaries. Electrochemical
parameters were in a good correlation with the results of NAML tests, which in turn,
confirmed the superiority of ARB multilayered structure over conventional cold rolled structure in terms of IGC susceptibility and corrosion stability.
Authors Key words
Al-Mg legura, hladno valjanje, akumulativno spajanje valjanjem,
mehanička svojstva, intergranularna korozija, β-faza
Authors Key words
Al-Mg alloy, cold rolling, accumulative roll bonding (ARB), mechanical properties, intergranular corrosion (IGC), β-phase
Type
Tekst
Abstract (sr)
Ispitivan je uticaj akumulativnog spajanja valjanjem (ARB postupak) i konvencionalnog hladnog valjanja (CR postupak) na mehanička i koroziona svojstva standardne AA5083 legure sa 4.2 mas. % Mg i modifikovane legure, sa sadržajem Mg od 5.1 mas.% i dodatkom 0.5 mas.% Zn. Rezultati ispitivanja jednoosnim zatezanjem pokazali su da dolazi do značajnog povećanja parametara čvrstoće i smanjenja
izduženja nakon svakog ARB provlaka i sa porastom stepena deformacije CR postupkom. Pokazana je prednost ARB postupka nad klasičnim postupkom hladnog
valjanja obzirom da se mogu postići veći stepeni deformacije i veća rafinacija strukture.
Pokazano je da povišen sadržaj Mg doprinosi porastu čvrstoće, dok se potencijal za ojačavanje i koroziona otpornost smanjuju. Viši nivo čvrstoće CR traka rezultat je veće gustine dislokacija i izraženijeg deformacionog ojačavanja zbog intenzivnije interakcije dislokacija kod konvencionalnog valjanja u odnosu na ARB postupak. Rezultati testa gubitka mase (NAMLT) pokazali su otpornost jednoslojnih CR i višeslojnih ARB traka ispitivanih legura prema intergranularnoj koroziji (IGC) u deformisanom stanju. Međutim, nakon 7 dana senzitizacije na 100 i 150 °C, CR uzorci AA5083 legure postaju
osetljivi, dok ARB uzorci ostaju otporni prema IGC. Za razliku od standardne legure, CR i ARB trake modifikovane legure pokazale su veliku osetljivost prema IGC nakon tretmana senzitizacije. Osetljivost prema IGC u korelaciji je sa različitom morfologijom i raspodelom β-faze (Mg2Al3) istaložene tokom senzitizacije. Otkriveno je da postojanje smicajnih traka usled intenzivne plastične deformacije u višeslojnoj ARB strukturi, i
pasivnog filma između slojeva doprinosi povoljnoj raspodeli β-faze u strukturi otpornih ARB uzoraka što su potvrdili i rezultati elektrohemijskih ispitivanja. U slučaju IGC osetljivih CR uzoraka, velika količina β-faze istaložena je duž granica zrna.
Elektrohemijski parametri su u dobroj korelaciji sa rezultatima NAML testa, koji su
potvrdili prednost ARB višeslojne strukture u odnosu na konvencionalno hladno
valjanu, i ustanovljeno je da ARB postupak ima realnu mogućnost praktične industrijske
primene za izradu višeslojnih traka jer omogućava transformaciju Al-Mg legura u materijale novih, pobolјšanih svojstava.
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.