Title
Sinteza, strukturne i optičke osobine itrijum-hafnata, itrijum-cirkonata i itrijum-stanata dopiranih jonima europijuma
Creator
Papan, Jelena, 1989-
Copyright date
2018
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 06.07.2018.
Other responsibilities
mentor
Roglić, Goran, 1964-
mentor
Dramićanin, Miroslav.
član komisije
Jovanović, Dragana.
član komisije
Nikolić, Aleksandar.
član komisije
Manojlović, Dragan, 1961-
Academic Expertise
Prirodno-matematičke nauke
Academic Title
-
University
Univerzitet u Beogradu
Faculty
Hemijski fakultet
Alternative title
Synthesis, structural and optical properties of yttrium-hafnate, yttrium-zirconate and yttrium-stanate doped with europium ions
Publisher
[ J. Papan]
Format
142 lista
description
Prirodno-matematičke nauke - Primenjena hemija / Life sciences - Applied chemistry
Abstract (sr)
U okviru ove doktorske disertacije sintetisani su neorganski luminescentni materijali opšte formule A2B2O7 (A3+, B4+) na bazi itrijum-hafnata (Y2Hf2O7), itrijum-cirkonata (Y2Zr2O7) i itrijum-stanata (Y2Sn2O7) i koji su dopirani jonima europijuma (Eu3+) u širokim opsezima koncentracija. Materijali su sintetisani metodom termalne dekompozicije uz korišćenje PEG-a kao goriva i ko-precipitacionom tehnikom uz dodatno žarenje na optimalnoj temperaturi u vremenskom intervalu od 24 sata. Dopiranje je izvršeno u opsegu 0≤ x ≤ 1 za sisteme Y2-xEuxHf2O7 i Y2-xEuxZr2O7 i u opsegu 0≤ x ≤ 0,6 za sistem Y2-xEuxSn2O7 (gde je x udeo Eu3+ jona). Sintetisani su i uzorci kod kojih je jon itrijuma (A3+ = Y3+) potpuno zamenjen jonima gadolinijuma (Gd3+) i lutecijuma (Lu3+) pri čemu je koncentracija europijuma bila konstantna. Svi uzorci su kristalisali u defektno fluoritnu fazu prostorne grupe Fm3̅m. Dobijene su čestice nanodimenzija, pretežno kockastog oblika. Detaljno su ispitivane optičke osobine. Sve ispitivane uzorke karakteriše efikasna apsorpcija na 464 nm i dominatna emisija u crvenom delu spektra na oko 612 nm. Određena su vremena života, kritična rastojanja, tip multipolarnih interakcija odgovornih za gašenje signala i matematički su definisane boje. Džud-Ofeltovom analizom je utvrđeno da povećanje procenta dopiranja dovodi do smanjenja asimetričnog odnosa što ukazuje da okruženje oko jona dopanta (Eu3+) sa povećanjem procenta dopiranja postaje simetričnije. Neke od ispitivanih uzoraka karakteriše i jako visoka kvantna efikasnost ( > 90%) što je izuzetno bitno za eventualnu komercijalnu primenu.
Abstract (en)
Within this doctoral thesis, synthesized samples are inorganic luminescent materials, with general formula A2B2O7 (A3+, B4+), bazed on yttrium-hafnate (Y2Hf2O7), yttrium-zirconate (Y2Zr2O7 ) and yttrium-stanate (Y2Sn2O7) doped with europium ions, in wide concentration range. These materials were synthesized by PEG and co-precipitation method, at optimal temperature, for 24 h. Also, one part of obtained samples are samples where are yttrium ions (Y3+) completely exchanged with gadolinium ions (Gd3+) and lutetium ions (Lu3+), where concentration of europium is constant (1 at. Eu3+). Samples are doped in range 0≤ x ≤ 1 in systems Y2-xEuxHf2O7 and Y2-xEuxZr2O7, and in range 0≤ x ≤ 0,6 in system Y2-xEuxSn2O7 (where x is atomic percentage of Eu3+). All samples are crystalited in defect-flurite phase, with space group Fm3̅m. Obtained particles have nanodimensions, predominantly round-cube shape. Detailed study of optical properties is examined. Studied samples had caracteristic effective absorption at 464 nm, with a red emission of about 612 nm. Determined parameters are: life time, critical distance, type of multipolar interactions responsable for signal quenching and emitting colors are matematicaly defined. Judd-Ofelt analysis showed that doping increases the asymmetric ratio, which indicates that the dopant environment (Eu3+) with more doping becomes more symmetrical. Some of the tested samples are characterized by very high quantum efficiency ( > 90%) which is important for possible commercial application.
Authors Key words
Itrijum-hafnat / itrijum-cirkonat / itrijum-stanat / jon europijuma / neorganski luminescentni materijali
Authors Key words
yttrium-hafnate / yttrium-zirconate / yttrium-stanate / europium ion / inorganic luminescent materials
Type
Tekst
Abstract (sr)
U okviru ove doktorske disertacije sintetisani su neorganski luminescentni materijali opšte formule A2B2O7 (A3+, B4+) na bazi itrijum-hafnata (Y2Hf2O7), itrijum-cirkonata (Y2Zr2O7) i itrijum-stanata (Y2Sn2O7) i koji su dopirani jonima europijuma (Eu3+) u širokim opsezima koncentracija. Materijali su sintetisani metodom termalne dekompozicije uz korišćenje PEG-a kao goriva i ko-precipitacionom tehnikom uz dodatno žarenje na optimalnoj temperaturi u vremenskom intervalu od 24 sata. Dopiranje je izvršeno u opsegu 0≤ x ≤ 1 za sisteme Y2-xEuxHf2O7 i Y2-xEuxZr2O7 i u opsegu 0≤ x ≤ 0,6 za sistem Y2-xEuxSn2O7 (gde je x udeo Eu3+ jona). Sintetisani su i uzorci kod kojih je jon itrijuma (A3+ = Y3+) potpuno zamenjen jonima gadolinijuma (Gd3+) i lutecijuma (Lu3+) pri čemu je koncentracija europijuma bila konstantna. Svi uzorci su kristalisali u defektno fluoritnu fazu prostorne grupe Fm3̅m. Dobijene su čestice nanodimenzija, pretežno kockastog oblika. Detaljno su ispitivane optičke osobine. Sve ispitivane uzorke karakteriše efikasna apsorpcija na 464 nm i dominatna emisija u crvenom delu spektra na oko 612 nm. Određena su vremena života, kritična rastojanja, tip multipolarnih interakcija odgovornih za gašenje signala i matematički su definisane boje. Džud-Ofeltovom analizom je utvrđeno da povećanje procenta dopiranja dovodi do smanjenja asimetričnog odnosa što ukazuje da okruženje oko jona dopanta (Eu3+) sa povećanjem procenta dopiranja postaje simetričnije. Neke od ispitivanih uzoraka karakteriše i jako visoka kvantna efikasnost ( > 90%) što je izuzetno bitno za eventualnu komercijalnu primenu.
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.