Title
Dobijanje nanostrukturnih prahova u cilju proizvodnje novih disperzno ojačanih sinterovanih materijala u sistemu Cu-Al2O3
Creator
Korać, Marija, 1978-
Copyright date
2009
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 29.12.2009.
Other responsibilities
mentor
Kamberović, Željko, 1968-
član komisije
Filipović, Mirjana, 1959-
član komisije
Talijan, Nadežda
Academic Expertise
Tehničko-tehnološke nauke
University
Univerzitet u Beogradu
Faculty
Tehnološko-metalurški fakultet
Alternative title
Obtaining of nanostructured powders for production of new dispersion strengthened sintered material in the system Cu-Al2O3
Publisher
[M. Korać]
Format
PDF/A (127 listova)
description
Metalurgija / Metallurgy
Abstract (sr)
U doktorskoj disertaciji je ispitivana mogućnost sinteze nanostrukturnih
kompozitnih materijala na bazi bakra i glinice novom metodom, koja predstavlja
kombinaciju termo-hemijskog postupka sinteze i mehaničkog legiranja. Termohemijska
sinteza se odvija kroz tri faze i to: sušenje raspršivanjem rastvora nitrata,
oksidaciono žarenje i redukcija. Metoda sinteze je razvijena sa ciljem dobijanja
materijala sa superiornijim osobinama u odnosu na konvencionalne.
U toku rada određeni su optimalni parametri procesa za svaku od faza sinteze,
kao i karkaterizacija praha prekursora dobijenog hemijskim putem i finalnog praha
dobijenog mehaničkim legiranjem različitim instrumentalnim metodama (SEM,
XRD i AEM).
Prahovi sa 1; 1,5 i 2% Al2O3 su sinterovani na različitim temperaturama u
opsegu od 725-925°C u toku 15-120 min sa ciljem optimizacije parametara procesa
sinterovanja dobijenih prahova. Određena je optimalna temperatura od 875°C i
vreme od 1h. U cilju potvrđivanja upotrebnih osobina materijala, sinterovani uzorci
su dalje mehanički i termički tretirani.
Dokazano je da termo-mehanički tretman ima pozitivan uticaj na
karakteristike materijala i kombinaciju električnih i mehaničkih svojstava koja se
zahteva od ove vrste materijala. Vrednosti električne provodljivosti nakon termomehaničkog
tretmana su na nivou od 61%IACS, a tvrdoće od 57HRF.
Na osnovu mikrostrukturnih analiza i merenja električne provodljivosti i
tvrdoće materijala, ojačavanje do kog dolazi u ispitivanom sistemu može biti
objašenjeno mehanizmom koji čine disperzno, deformaciono i ojačavanje
granicama zrna. Ojačavanje granicom zrna se postiže ne samo disperzoidom već i
novoformiranom trećom fazom koja je detektovana u strukturi, čime se sprečava
proces rasta zrna i povećava stabilnost materijala na povišenim temperaturama.
Prednost predložene metode dobijanja se ogleda u velikom potencijalu za
industrijsku proizvodnju i dobijanja značajnih količina prahova po relativno niskoj
ceni, zbog jednostavnosti procesa sinteze i korišćenja sirovina sa niskom cenom za
dobijanje materijala sa unapređenim osobinama.
Ova doktorska disertacija je urađena u okviru realizacije projekta tehnološkog
razvoja koje je finansiralo Ministarstvo za nauku i tehnološki razvoj Republike
Srbije evidencioni broj 19032 ”Dobijanje nanostrukturnih prahova u cilju
proizvodnje novih disperzno ojačanih sinterovanih materijala u sistemu Cu-Al2O3”
(2008-2010).
Abstract (en)
This PhD thesis presents the possibility of nanostructured composite materials
based on copper and alumina synthesis trough a new method, which is a
combination of thermo-chemical synthesis and mechanical alloying. Thermochemical
synthesis is carried out through three stages: spray drying of nitrate
solutions, oxidation and reduction. Synthesis method was developed with the aim of
obtaining materials with superior properties compared to conventional ones.
For each phase of synthesis process parameters were optimized.
Characterization of powder precursors obtained by chemical means and the final
powder obtained by mechanical alloying was carried out by different instrumental
methods (SEM, XRD and AEM).
Powders with 1, 1.5 and 2% Al2O3 were sintered at different temperatures in
the range of 725-925°C during 15-120min in order to optimize sintering process
parameters obtained. Optimal sintering temperature at 875°C was determined and
sintering time of 1h. In order to confirm utility properties, sintered samples were
further mechanically and thermally treated.
It is proven that the thermo-mechanical treatment has a positive influence on
the properties of materials and a combination of electrical and mechanical
properties that is required for this type of material. The values of electrical
conductivity after thermo-mechanical treatment on the level of 61% IACS, and the
hardness of 57HRF.
Based on microstructural analysis and measurements of electrical conductivity
and hardness of materials, reinforcement that appears in the examined system can
be explained by complex mechanism involving dispersive, deformation and grain
boundary strengthening. Grain boundary strengthening is achieved not only by
dispersoide, but by the newly formed third phase detected in the structure, which
prevents the process of grain growth and increases the stability of the material at
elevated temperatures.
The advantage of the proposed method is in it’s the great potential for
industrial production and production of significant amounts of powders at relatively
low cost because of the simplicity of the synthesis process and use of low cost raw
materials for production of materials with improved properties.
This PhD thesis is part of the technological development project funded by the
Ministry of Science and Technological Development of Serbia, No. 19032
”Obtaining of nanostructured powders for production of new dispersion
strengthened sintered material in the system Cu-Al2O3” (2008-2010).
Authors Key words
nanostrukturni prahovi, Cu-Al2O3, kontaktni materijali,
disperzno ojačavanje, ojačavanje granicama zrna, novi metod sinteze, hemijska
sinteza, mehaničko legiranje
Authors Key words
nanostructured powders, Cu-Al2O3, contact materials, dispersion
strengthening, grain boundaries strengthening, new synthesis method, chemical
synthesis, mechanical alloying
Classification
669-138:66.018(043.3)
Subject
Nanostrukturni materijali
Subject
Sinterovani materijali
Type
Tekst
Abstract (sr)
U doktorskoj disertaciji je ispitivana mogućnost sinteze nanostrukturnih
kompozitnih materijala na bazi bakra i glinice novom metodom, koja predstavlja
kombinaciju termo-hemijskog postupka sinteze i mehaničkog legiranja. Termohemijska
sinteza se odvija kroz tri faze i to: sušenje raspršivanjem rastvora nitrata,
oksidaciono žarenje i redukcija. Metoda sinteze je razvijena sa ciljem dobijanja
materijala sa superiornijim osobinama u odnosu na konvencionalne.
U toku rada određeni su optimalni parametri procesa za svaku od faza sinteze,
kao i karkaterizacija praha prekursora dobijenog hemijskim putem i finalnog praha
dobijenog mehaničkim legiranjem različitim instrumentalnim metodama (SEM,
XRD i AEM).
Prahovi sa 1; 1,5 i 2% Al2O3 su sinterovani na različitim temperaturama u
opsegu od 725-925°C u toku 15-120 min sa ciljem optimizacije parametara procesa
sinterovanja dobijenih prahova. Određena je optimalna temperatura od 875°C i
vreme od 1h. U cilju potvrđivanja upotrebnih osobina materijala, sinterovani uzorci
su dalje mehanički i termički tretirani.
Dokazano je da termo-mehanički tretman ima pozitivan uticaj na
karakteristike materijala i kombinaciju električnih i mehaničkih svojstava koja se
zahteva od ove vrste materijala. Vrednosti električne provodljivosti nakon termomehaničkog
tretmana su na nivou od 61%IACS, a tvrdoće od 57HRF.
Na osnovu mikrostrukturnih analiza i merenja električne provodljivosti i
tvrdoće materijala, ojačavanje do kog dolazi u ispitivanom sistemu može biti
objašenjeno mehanizmom koji čine disperzno, deformaciono i ojačavanje
granicama zrna. Ojačavanje granicom zrna se postiže ne samo disperzoidom već i
novoformiranom trećom fazom koja je detektovana u strukturi, čime se sprečava
proces rasta zrna i povećava stabilnost materijala na povišenim temperaturama.
Prednost predložene metode dobijanja se ogleda u velikom potencijalu za
industrijsku proizvodnju i dobijanja značajnih količina prahova po relativno niskoj
ceni, zbog jednostavnosti procesa sinteze i korišćenja sirovina sa niskom cenom za
dobijanje materijala sa unapređenim osobinama.
Ova doktorska disertacija je urađena u okviru realizacije projekta tehnološkog
razvoja koje je finansiralo Ministarstvo za nauku i tehnološki razvoj Republike
Srbije evidencioni broj 19032 ”Dobijanje nanostrukturnih prahova u cilju
proizvodnje novih disperzno ojačanih sinterovanih materijala u sistemu Cu-Al2O3”
(2008-2010).
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.