Title
Електричне особине композита изотактичког полипропилена (iPP) и атактичког полистирена (aPS) добијених третманом у растворима соли прелазних и алкалних метала
Creator
Петронијевић, Иван М., 1982- 21600615
Copyright date
2018
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 17.09.2018.
Other responsibilities
mentor
Cerović, Dragana, 1967- 21602919
član komisije
Dojčilović, Jablan, 1951- 2226279
član komisije
Popović, Dušan, 1966- 8020583
Academic Expertise
Prirodno-matematičke nauke
Academic Title
-
University
Univerzitet u Beogradu
Faculty
Fizički fakultet
Alternative title
Electrical properties of composites based on isotactic polypropylene (iPP) and atactic polystyrene (aPS) obtained in solutions of alkali and transition metal salts.
Publisher
[И. М. Петронијевић]
Format
`119 листова
description
Физика - Физика кондензоване материје и статистичка физика / Physics - Condensed matter physics and statistical physics
Abstract (sr)
У оквиру ове докторске дисертације је презентована нова, једноставна,
економична и еколошки прихватљива метода синтезе полимерних нанокомпозита.
Изотактички полипропилен (iPP) и атактички полистирен (aPS) су независно
потапани у три засићена водена раствора соли алкалних метала (LiCl, NaCl, и
KCl) и три засићена водена раствора соли прелазних метала (MnCl2, FeCl2, NiCl2)
на две температурe (23 ○C и 90 ○C) и на различитим DC електричним
потенцијалима (+4 kV, -4 kV и потенцијал земље). Присуство и концентрације
метала у полимерним матрицама одређени су ICP-OES. Добијене концентрације
се крећу у опсегу од 1,82·10-9 mol/cm3 до 1,17·10-5 mol/cm3. Методом TOF-SIMS
констатоване су одговарајућа дистрибуција и дисперзија, а помоћу ТЕМ-а уочене
су наночестице димензија од 3 nm до 20 nm, сферног облика са морфологијом
језгро-омотач. Компаративна анализа указала је на повезаност између вредности
ε’ и концентрација алкалних и прелазних метала у узорцима нанокомпозита.
Показано је да узорци са највећом концентарацијом метала имају и највише
вредности ε’ док узорци са најнижим концентрацијама имају најниже вредности
ε’. Поређене су температурно фреквентне зависности ε’ и tan δ нетретираних и
третираних узорака и констатовано је да су вредности ε’ у целом температурно
фреквентном опсегу више за нанокомпозите, док су вредности tan δ више за
нетретиране полимере. На основу струјно напонске карактеристике је закључено
да припремљени нанокомпозити показују веће вредности густине електричне
струје. Новом мерном експерименталном методом уведени су параметри
осетљивији на промене у електричним особинама полимерних материјала него
параметри ε’ и tan δ. Ова метода омогућава детектовање малих промена у
диелектричним особинама полимера, нанокомпозита полимера, као и код других
материјала.
Abstract (en)
In this dissertation, a new, simple, economical and environmentally friendly
method for the synthesis of polymer nanocomposites has been presented. Isotactic
polypropylene (iPP) and atactic polystyrene (aPS) were separately immersed in three
saturated water solutions of alkali metal salts (LiCl, NaCl, and KCl) and three saturated
water solutions of transition metals salts (MnCl2, FeCl2, NiCl2) at two temperatures
(23ºC and 90ºC) and three DC electrical potentials (+4 kV, -4 kV and ground
potential). The presence and quantification of metals in the polymer matrices were
carried out by ICP-OES. The obtained concentration values were from
1,82·10-9 mol/cm3 to 1,17·10-5 mol/cm3. By the TOF-SIMS method, an appropriate
distribution and dispersion were established. By the TЕМ method, spherical
nanoparticles with core-shell morphology with dimensions from 3 nm to 20 nm in
diameter have been determined. A comparative analysis showed the connection between
values of ε’ and concentration of metals in the nanocomposite samples. It has been
shown that samples with the highest concentrations of metal have the highest values of
ε’, while the samples with the lowest concentrations have the lowest values of ε’.
Temperature frequency dependence analysis of ε’ and tan δ of untreated and treated
samples was conducted and it was found that the values of ε’ in whole temperature
frequency range are higher for nanocomposites, while tan δ are higher for untreated
polymers. Based on the current-voltage characteristics, it was concluded that the
prepared nanocomposites show higher values of the electrical current density. The new
measurement experimental method introduced parameters more sensitive to changes in
the electrical properties then ε’ and tan δ. This method allows detection of small
changes in the dielectric properties of the polymer, polymer nanocomposites, and other
materials.
Authors Key words
електричне особине, диелектрична спектроскопија, полимерни
нанокомпозити
Authors Key words
electric properties, dielectric spectroscopy, polymer nanocomposites
Type
Tekst
Abstract (sr)
У оквиру ове докторске дисертације је презентована нова, једноставна,
економична и еколошки прихватљива метода синтезе полимерних нанокомпозита.
Изотактички полипропилен (iPP) и атактички полистирен (aPS) су независно
потапани у три засићена водена раствора соли алкалних метала (LiCl, NaCl, и
KCl) и три засићена водена раствора соли прелазних метала (MnCl2, FeCl2, NiCl2)
на две температурe (23 ○C и 90 ○C) и на различитим DC електричним
потенцијалима (+4 kV, -4 kV и потенцијал земље). Присуство и концентрације
метала у полимерним матрицама одређени су ICP-OES. Добијене концентрације
се крећу у опсегу од 1,82·10-9 mol/cm3 до 1,17·10-5 mol/cm3. Методом TOF-SIMS
констатоване су одговарајућа дистрибуција и дисперзија, а помоћу ТЕМ-а уочене
су наночестице димензија од 3 nm до 20 nm, сферног облика са морфологијом
језгро-омотач. Компаративна анализа указала је на повезаност између вредности
ε’ и концентрација алкалних и прелазних метала у узорцима нанокомпозита.
Показано је да узорци са највећом концентарацијом метала имају и највише
вредности ε’ док узорци са најнижим концентрацијама имају најниже вредности
ε’. Поређене су температурно фреквентне зависности ε’ и tan δ нетретираних и
третираних узорака и констатовано је да су вредности ε’ у целом температурно
фреквентном опсегу више за нанокомпозите, док су вредности tan δ више за
нетретиране полимере. На основу струјно напонске карактеристике је закључено
да припремљени нанокомпозити показују веће вредности густине електричне
струје. Новом мерном експерименталном методом уведени су параметри
осетљивији на промене у електричним особинама полимерних материјала него
параметри ε’ и tan δ. Ова метода омогућава детектовање малих промена у
диелектричним особинама полимера, нанокомпозита полимера, као и код других
материјала.
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.