Title
Kristalna struktura i električne karakteristike BaTi1-xSnxO3 i CaCuTi4-xRuxO12 perovskitnih materijala
Creator
Veselinović, Ljiljana. 1975-
Copyright date
2016
Object Links
Select license
Autorstvo-Nekomercijalno-Bez prerade 3.0 Srbija (CC BY-NC-ND 3.0)
License description
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Committee report
Theses Type
Doktorska disertacija
description
Datum odbrane: 27.09.2016.
Other responsibilities
mentor
Cvjetićanin, Nikola, 1959-
mentor
Marković, Smilja, 1968-
član komisije
Mitrić, Miodrag
član komisije
Damjanović, Ljiljana, 1971-
Academic Expertise
Prirodno-matematičke nauke
Academic Title
-
University
Univerzitet u Beogradu
Faculty
Fakultet za fizičku hemiju
Alternative title
Crystal structure and electrical properties of BaTi1-xSnxO3 and CaCu3Ti4-xRuxO12 perovskites materialas.
Publisher
[Lj. Veselinović]
Format
VI, 127 listova, VI
description
Fizička hemija - Nauka o materijalima / Physical chemistry - Materials science
Abstract (sr)
U cilju uspostavljanja korelacije faznih transformacija i relativne dielektrične
permitivnosti perovskita ABX3 tipa i složenih perovskita AC3B4O12 tipa, detaljno su
proučeni fazni sastav i kristalna struktura BaTi1 xSnxO3 i CaCu3Ti4-xRuxO12 materijala.
Struktura barijum titanat stanatnih BaTi1 xSnxO3 (BTS) (x=0; 0,025; 0,05; 0,07; 0,10;
0,12; 0,15 i 0,20) prahova analizirana je na sobnoj temperaturi uz pomoć rendgenske
difrakcione analize (XRD), transmisione elektronske mikroskopije (TEM), visoko
rezolucione transmisione elektronske mikroskopije (HRTEM), elektronske difrakcije sa
odabrane površine (SAED), kao i ramanske spektroskopske analize. Rezultati
Ritveldove analize, primenjene na podatke prikupljene rendgenskom difrakcijom sa
polikristalnih materijala, pokazali su da postepena zamena jona titanijuma jonima kalaja
u BaTiO3 perovskitima, dovodi do faznih transformacija od tetragonalne za 0x0,07
do kubne za x= 0,12; 0,15 i 0,20. Koegzistencija tetragonalne (P4mm) i kubne (Pm 3 m)
kristalne faze utvrđena je kod praha sa nominalnim sastavom BaTi0,9Sn0,1O3. Promene
kristalne strukture određene na osnovu Ritveldovog utačnjavanja potvrđene su HRTEM
i SAED analizom. Za analizu lokalnog uređenja proučavanih prahova korišćena je
Ramanska spektroskopija. Dobijeni rezultati pokazali su prisustvo tetragonalne (P4mm)
i malog procenta ortorombične (Amm2) kristalne faze za sve ispitivane BTS prahove što
ukazuje na nižu lokalnu simetriju. U cilju preciznijeg određivanja kristalne strukture
BTS prahova u daljem radu je korišćena metoda neutronske difrakcije sa polikristalnih
materijala (NPD). Podaci prikupljeni neutronskom difrakcijom sa polikristalnih
BaTi1 xSnxO3 prahova (x=0, 0,025; 0,05; 0,07; 0,10; 0,12; 0,15 i 0,20) na sobnoj
temperaturi utačnjeni su primenom Ritveldove metode. Dobijeni rezultati potvrdili su da
prah barijum titanata (x=0) kristališe tetragonalno u P4mm prostornoj grupi. Kristalna
struktura serije čvrstih rastvora BaTi1 xSnxO3 kod kojih je 0,025 ≤ x ≤ 0,07 utačnjena je
kao dvofazni sistem tetragonalne P4mm i ortorombične Amm2 faze, dok prahovi kod
kojih je x=0,10 i 0,12 pokazuju koegzistenciju romboedarske R3m i kubne Pm3 m faze...
Abstract (en)
In order to establish a correlation of phase transformations with relative
dielectric permitivity of the ABX3 perovskites and double AC3B4O12 perovskites, phase
composition and crystal structure of the BaTi1 xSnxO3 and CaCu3Ti4-xRuxO12 materials,
were examined in details. The influence of Sn for Ti substitution on the crystal structure
of barium titanate stannate (BTS) BaTi1 xSnxO3 (x = 0, 0.025, 0.05, 0.07, 0.10, 0.12,
0.15 and 0.20) was investigated. The powders were prepared by conventional solid state
reaction technique. The structural investigations of the BTS powders were done at room
temperature by X-ray powder diffraction (XRD), transmission electron microscopy
(TEM), high-resolution TEM (HRTEM), selected area electron diffraction (SAED), as
well as Raman spectroscopy analyses. Rietveld refinement of XRD data indicates that
gradual replacement of titanium by tin in BaTiO3 provokes phase transition from
tetragonal for 0x0.07 to cubic for x= 0.12, 0.15 and 0.20. Coexistence of tetragonal
(P4mm) and cubic (Pm 3 m) crystal phases was found in powder with BaTi0.9Sn0.1O3
nominal composition. The crystal phases determined by Rietveld refinement were
confirmed by HRTEM and SAED analyses. The crystal structures of BTS powders at
middle-range scale were studied by Raman spectroscopy which shows tetragonal
(P4mm) and small fraction of orthorhombic (Pmm2) crystal phases for all the examined
BTS powders, implying the lower local ordering when compared to average symmetry.
In order to provide a more precise determination of BTS crystal structures the neuton
powder difraction (NPD) was used. The room temperature phase composition and
crystal structures of BTS samples with x = 0, 0.025, 0.05, 0.07, 0.10, 0.12, 0.15 and 0.20
were determined by Rietveld refinement of NPD data. The crystal structure of the
barium titanate sample (x=0) crystallizes in the well-known tetragonal P4mm space
group. The crystal structure of the samples with 0.025≤x≤ 0.07 were refined as mixtures
of P4mm and Amm2 phases; those with x = 0.10 and 0.12 show the coexistence of
rhombohedral R3m and cubic Pm3m phases, while the samples with x=0.15 and 0.20
crystallize in a single cubic Pm3m phase. Temperature-dependent NPD was used to
characterize the BaTi0.95Sn0.05O3 sample at 0, 60, and 100 °C which was found to form
single phase Amm2, P4mm, and Pm3m structures at these temperatures, respectively...
Authors Key words
Barijum titanat stanati, kalcijum bakar titanijum oksidi, električne karakteristike, neutronska
difrakcija, rendgenska difrakcija, Ritveldova analiza
Authors Key words
Barium titanat stanate, Calcium copper titanium oxide, electrical properties, X-ray
powder diffracion, Neutron powder diffraction, Rietveld refinement
Type
Tekst
Abstract (sr)
U cilju uspostavljanja korelacije faznih transformacija i relativne dielektrične
permitivnosti perovskita ABX3 tipa i složenih perovskita AC3B4O12 tipa, detaljno su
proučeni fazni sastav i kristalna struktura BaTi1 xSnxO3 i CaCu3Ti4-xRuxO12 materijala.
Struktura barijum titanat stanatnih BaTi1 xSnxO3 (BTS) (x=0; 0,025; 0,05; 0,07; 0,10;
0,12; 0,15 i 0,20) prahova analizirana je na sobnoj temperaturi uz pomoć rendgenske
difrakcione analize (XRD), transmisione elektronske mikroskopije (TEM), visoko
rezolucione transmisione elektronske mikroskopije (HRTEM), elektronske difrakcije sa
odabrane površine (SAED), kao i ramanske spektroskopske analize. Rezultati
Ritveldove analize, primenjene na podatke prikupljene rendgenskom difrakcijom sa
polikristalnih materijala, pokazali su da postepena zamena jona titanijuma jonima kalaja
u BaTiO3 perovskitima, dovodi do faznih transformacija od tetragonalne za 0x0,07
do kubne za x= 0,12; 0,15 i 0,20. Koegzistencija tetragonalne (P4mm) i kubne (Pm 3 m)
kristalne faze utvrđena je kod praha sa nominalnim sastavom BaTi0,9Sn0,1O3. Promene
kristalne strukture određene na osnovu Ritveldovog utačnjavanja potvrđene su HRTEM
i SAED analizom. Za analizu lokalnog uređenja proučavanih prahova korišćena je
Ramanska spektroskopija. Dobijeni rezultati pokazali su prisustvo tetragonalne (P4mm)
i malog procenta ortorombične (Amm2) kristalne faze za sve ispitivane BTS prahove što
ukazuje na nižu lokalnu simetriju. U cilju preciznijeg određivanja kristalne strukture
BTS prahova u daljem radu je korišćena metoda neutronske difrakcije sa polikristalnih
materijala (NPD). Podaci prikupljeni neutronskom difrakcijom sa polikristalnih
BaTi1 xSnxO3 prahova (x=0, 0,025; 0,05; 0,07; 0,10; 0,12; 0,15 i 0,20) na sobnoj
temperaturi utačnjeni su primenom Ritveldove metode. Dobijeni rezultati potvrdili su da
prah barijum titanata (x=0) kristališe tetragonalno u P4mm prostornoj grupi. Kristalna
struktura serije čvrstih rastvora BaTi1 xSnxO3 kod kojih je 0,025 ≤ x ≤ 0,07 utačnjena je
kao dvofazni sistem tetragonalne P4mm i ortorombične Amm2 faze, dok prahovi kod
kojih je x=0,10 i 0,12 pokazuju koegzistenciju romboedarske R3m i kubne Pm3 m faze...
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.