Title
Karakteristike polimetil-metakrilata sa dodatkom nanočestica cink-oksida u izradi totalnih zubnih proteza
Creator
Popović, Danica, 1984-, 32857703
Copyright date
2018
Object Links
Select license
Autorstvo-Bez prerade 3.0 Srbija (CC BY-ND 3.0)
License description
Dozvoljavate umnožavanje, distribuciju i javno saopštavanje dela, bez promena, preoblikovanja ili upotrebe dela u svom delu, ako se navede ime autora na način odredjen od strane autora ili davaoca licence. Ova licenca dozvoljava komercijalnu upotrebu dela. Osnovni opis Licence: http://creativecommons.org/licenses/by-nd/3.0/rs/deed.sr_LATN Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nd/3.0/rs/legalcode.sr-Latn
Language
Serbian
Cobiss-ID
Theses Type
Doktorska disertacija
description
Datum odbrane: 17.12.2018.
Other responsibilities
mentor
Lazić, Vojkan, 1963-, 12627047
mentor
Rudolf, Rebeka, 1969-, 8811623
član komisije
Obradović-Đuričić, Kosovka, 1956-, 12462695
član komisije
Đorđević, Igor, 1972-, 34631783
član komisije
Raić, Karlo, 1955-, 12444775
Academic Expertise
Medicinske nauke
University
Univerzitet u Beogradu
Faculty
Stomatološki fakultet
Alternative title
Characteristics of polymethyl-methacrylate enriched with zinc-oxide nanoparticles in complete dentures
Publisher
[D. F. Popović]
Format
131 list
description
Stomatologija - Stomatološka protetika / Dentistry - Prosthodontics
Abstract (sr)
Doktorska disertacija se bavi sintezom novog kompozita polimetil-metakrilata (PMMA) obogaćenog sferičnim nanočesticama cink-oksida (ZnO Nč), tehnikama karakterizacije i analizom dobijenih rezultata.
Postavljena je hipoteza da totalne zubne proteze (TZP) izrađene od PMMA obogaćenog ZnO Nč mogu imati bolje fizičke i mehaničke karakterisatike u odnosu na TZP izrađene od konvencionalnog PMMA.
U cilju potvrde postavljene hipoteze ove doktorske disertacije u prvom delu istraživanja je sintetisan novi kompozit PMMA/ZnO Nč, sa različitim zapreminskim delovima ZnO nanočestica (2 i 3 vol.%) u matriksu PMMA. Metodom dinamičkog rasejavanja svetlosti (DLS) izmerena je distribucija ZnO Nč u matrixu PMMA. Istraživanje je sprovedeno na pločicama dimenzija 42 mm x 7 mm x 3 mm, kojima je prvo određena gustina piknometrom. Na uzorcima je odrađena mikrostrukturna karakterizacija uz pomoć metoda: skenirajuće elektronske mikroskopije (SEM), energijski disperzivne rendgenske spektroskopije (EDX), Zeta Potencijala, termogravimetrijske analize (TGA), dinamičke mehaničke analize (DMA), flash diferencijalne skenirajuće kalorimetrije (Flash DSC), a kao kontrola su korišćeni uzorci čistog PMMA.
Na osnovu dobijenih rezultata i njihove analize iz prvog dela istraživanja urađeni su konkretni modeli zuba (oblika prvog gornjeg stalnog kutnjaka) i TZP kako bi se identifikovala mehanička svojstva koja su potrebna u kliničkoj praksi. Dobijeni uzorci su bili testirani na otpornost na habanje korišćenjem simulatora žvakanja i otpornost na lom sa klasičnim mehaničkim testom opterećenja.
Prvom analizom je dobijen uvid u mikrostrukturu novog kompozita PMMA/ZnO Nč prateći distribuciju ZnO Nč u matriksu PMMA. U suspenziji metil-metakrilata (MMA) sa ZnO Nč prosečna vrednost veličine nanočestica bila je 2.21± 0.10 μm, ali 42.1% nanočestica je bilo u opsegu 21,04 nm...
Abstract (en)
The Doctoral Dissertation presents the development and synthesis of a new composite material, polymethyl-methacrylate (PMMA), enriched with spherical zinc-oxide nanoparticles (ZnO NPs), characterization techniques, and analyses of the results.
The work hypothesis was that acrylic dentures made by PMMA enriched with ZnO NPs could have better physical and mechanical properties than dentures made by pure PMMA.
To confirm this thesis in the first part of the investigation, a new composite, PMMA/ZnO NPs, was synthesised and tested with a different volume fraction (2 and 3 vol.%) of these nanoparticles into a matrix of PMMA. The DLS technique was used for chaking ZnO NPs' distribution into a PMMA matrix. Investigation was done on samples, in the shape of laminae with dimensions 42 mm x 7 mm x 3 mm, on which density had first measured with a picnometer. Microstructural characterization was made - SEM, EDX, Zeta Potential, TGA, DMA, Flash DSC) and, as a control, samples were made from pure PMMA.
According to the results from the first part of the investigation, in the second step a concrete samples of a real model of teeth (in the shape of the first upper molar) and complete dentures had made, to identify which mechanical properties are required in clinical practice. These samples were tested for a wear resistance in a chewing simulator and for a fracture resistance in a classical mechanical tensile strength test.
With the first analysis an insight was got into the microstructure of the new composite material PMMA/ZnO NPs, and followed the distribution of these nanoparticles in the PMMA matrix. In suspension with MMA, the average value of ZnO NPs was 2.21± 0.10 μm, but 42.1% of the nanoparticles were around 21,04 nm. The problem with irregular distribution was solved with a different kind of mixture dry phase (PMMA powder and powder of ZnO NPs) for a 2h in contolled vacuum conditions for a precise synthesis of the new material. Density measurement in a new composite confirmed indirectly the loss of residual monomer, the most often the cause of allergyc reaction and porosity, which could lead to worse mechanical properties...
Authors Key words
PMMA, ZnO nanočestice, kompoziti, mikrostruktura, karakterizacija, totalne zubne proteze, otpornost na habanje, otpornost na lom
Authors Key words
PMMA, ZnO NPs, composite, microstructure, characterization, complete acrylic denture, wear resistance, fracture resistance
Classification
616.314-089.28(043.3)
Type
Tekst
Abstract (sr)
Doktorska disertacija se bavi sintezom novog kompozita polimetil-metakrilata (PMMA) obogaćenog sferičnim nanočesticama cink-oksida (ZnO Nč), tehnikama karakterizacije i analizom dobijenih rezultata.
Postavljena je hipoteza da totalne zubne proteze (TZP) izrađene od PMMA obogaćenog ZnO Nč mogu imati bolje fizičke i mehaničke karakterisatike u odnosu na TZP izrađene od konvencionalnog PMMA.
U cilju potvrde postavljene hipoteze ove doktorske disertacije u prvom delu istraživanja je sintetisan novi kompozit PMMA/ZnO Nč, sa različitim zapreminskim delovima ZnO nanočestica (2 i 3 vol.%) u matriksu PMMA. Metodom dinamičkog rasejavanja svetlosti (DLS) izmerena je distribucija ZnO Nč u matrixu PMMA. Istraživanje je sprovedeno na pločicama dimenzija 42 mm x 7 mm x 3 mm, kojima je prvo određena gustina piknometrom. Na uzorcima je odrađena mikrostrukturna karakterizacija uz pomoć metoda: skenirajuće elektronske mikroskopije (SEM), energijski disperzivne rendgenske spektroskopije (EDX), Zeta Potencijala, termogravimetrijske analize (TGA), dinamičke mehaničke analize (DMA), flash diferencijalne skenirajuće kalorimetrije (Flash DSC), a kao kontrola su korišćeni uzorci čistog PMMA.
Na osnovu dobijenih rezultata i njihove analize iz prvog dela istraživanja urađeni su konkretni modeli zuba (oblika prvog gornjeg stalnog kutnjaka) i TZP kako bi se identifikovala mehanička svojstva koja su potrebna u kliničkoj praksi. Dobijeni uzorci su bili testirani na otpornost na habanje korišćenjem simulatora žvakanja i otpornost na lom sa klasičnim mehaničkim testom opterećenja.
Prvom analizom je dobijen uvid u mikrostrukturu novog kompozita PMMA/ZnO Nč prateći distribuciju ZnO Nč u matriksu PMMA. U suspenziji metil-metakrilata (MMA) sa ZnO Nč prosečna vrednost veličine nanočestica bila je 2.21± 0.10 μm, ali 42.1% nanočestica je bilo u opsegu 21,04 nm...
“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.